Abstract:Co 3 O 4 nanorods, nanobelts, nanosheets and cubic/octahedral nanoparticles have been successfully synthesized with tunable size from the nanoscale to the microscale, accompanied by a variation in the nature of the exposed crystal planes. The products are formed by thermal treatment of Co(CO 3 ) 0.5 (OH)· 0.11 H 2 O nanorod, nanobelt, nanosheet and nanocubic/nanooctahedral precursors at 250 °C. Detailed characterization, including X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray photo-electron spectroscopy (XPS), and nitrogen adsorption and desorption isotherms, revealed that the as-prepared nanorods, nanobelts, and nanosheet Co 3 O 4 samples are single crystalline and mesoporous in nature with a predominance of exposed high-energy (110) crystal planes. They exhibited excellent electrochemical properties in supercapacitors, showing higher capacitance and better rate capability than conventional cubic/octahedral Co 3 O 4 nanoparticles having exposed low-energy (100) and (111) planes. No decay in capacitance was observed when the scan rate was increased from 5 mV/s to 100 mV/s, or from 1 A/g to 10 A/g. The maximum value of the specific capacitance was calculated to be 162.8 F/g and the capacitance retention reached as high as 90%. Their excellent performance in supercapacitors is believed to result from the large-area exposure of active (110) crystal planes. The Co 3 O 4 nanosheets showed the best performance due to their larger surface area and ability to provide a better pathway for charge transfer, and are promising electrode materials for application in practical supercapacitors.

Shape Versus Porosity: A Systematic Survey of Cobalt Oxide Nanosheet Calcination from 200 to 900°C

Effect of Calcination Temperature on the Porous Structure of Cobalt Oxide Micro-Flowers

Studies on the nanocrystalline Co3O4 by wet synthesis and its microstructure

Study on the structure and supercapacitive properties of Mesoporous Co3 O4 nanosheets

Shape Control of Cobalt Carbonate Particles by a Hydrothermal Process in a Mixed Solvent: an Efficient Precursor to Nanoporous Cobalt Oxide Architectures and Their Sensing Property

Enhancing Capacitance Behaviour Of Coooh Nanostructures Using Transition Metal Dopants By Ambient Oxidation

One-Pot Synthesis Of Porous Nickel Cobalt Sulphides: Tuning The Composition For Superior Pseudocapacitance

Porous Co3o4 Microcubes: Hydrothermal Synthesis, Catalytic and Magnetic Properties

Hydrothermal Synthesis of Cobalt Sulfide Nanotubes: the Size Control and Its Application in Supercapacitors

Preparation of Mesoporous Co3O4 Nanoparticles Via Solid−Liquid Route and Effects of Calcination Temperature and Textural Parameters on Their Electrochemical Capacitive Behaviors

Controllable hydrothermal-assisted synthesis of mesoporous Co3O4 nanosheets

Synthesis and Electrochemical Properties of Sticktight-Like and Nanosheet Co3o4 Particles

Porous cobalt oxides with tunable hierarchical morphologies for supercapacitor electrodes

Correlation Between Microstructure and Electrochemical Behavior of the Mesoporous Co3O4 Sheet and Its Ionothermal Synthesized Hydrotalcite-like Α-Co(oh)2 Precursor

Fabrication of porous Co3O4 with different nanostructures by solid-state thermolysis of metal–organic framework for supercapacitors

Synthesis Temperature Dependence of Morphologies and Properties of Cobalt Oxide and Silicon Nanocrystals

Facile hydrothermally grown cobalt oxide (Co 3 O 4 ) nanostructures and their electrochemical performances

An in Situ Dealloying and Oxidation Route to Co3O4 Nanosheets and Their Ambient‐Temperature CO Oxidation Activity

Microstructural and electrochemical properties of Co3O4 porous nanospheres

Controllable synthesis of Co 3 O 4 from nanosize to microsize with large-scale exposure of active crystal planes and their excellent rate capability in supercapacitors based on the crystal plane effect

Synthesis of Porous Co3O4 Nanoflake Array and Its Temperature Behavior As Pseudo-Capacitor Electrode