Abstract:The microstructure evolutions of nickel-based single crystal superalloy DD5 after solution treatment at different temperatures as well as heat treated with various routes were systematically investigated by differential scanning calorimeter (DSC), optical microscope (OM), scanning electron microscope (SEM) and electron probe microanalyzer (EPMA). The formation and elimination mechanisms of unfavorable incipient melting microstructure emerged during heat treatment were explored in detail. Microstructure observations reveal that a higher solution temperature can speed up the element diffusion, resulting in a more uniform element distribution. A reduced degree of lattice mismatch between γ phase and γ' phase would be obtained, which leads to an increase in the average size and content of γ' phase. However, excessively high solution temperature would cause the pre-melting occurred at the interface of γ matrix and γ' phase, causing the formation of incipient melting microstructure. The incipient melting microstructure can be eliminated by the subsequent homogenization process under the conditions that the solution temperature exceeds the solvus temperature of γ' phase. The formation course of incipient melting microstructure includes the pre-melting at the interface of γ matrix and γ' phase, the expansion of molten liquid, and the formation by the resolidification of molten liquid. The elimination of incipient melting microstructure begins with the dissolution of fine eutectic, followed by the dissolution of coarse γ' phase and the filling of pores, and eventually the dissolution of residual eutectic. Compared with standard heat treatment, remelting heat treatment can provide better homogenization effect of element for DD5 superalloy.

The Effect of Elemental Vaporization and Redistribution During Sub-Solvus Recrystallization of A Single Crystal Superalloy

Effect of Directional Solidification Methods on Solid Solution Window in Ni-based Single-Crystal Superalloy

The Effect of Post-heat Treatment on the Microstructures of Single Crystal DD6 Superalloy

Kinetics of Cellular Discontinuous Precipitation in A Re-Containing Single Crystal Superalloy

Directional Migration Behavior of Alloying Elements in the Rafting Process of the Single Crystal Superalloy Dd6

Sub-solvus Cellular Recrystallization and P Phase Formation in a Single-Crystal Superalloy Containing Re

Microstructural Evolution on the Initiation of Sub-Solvus Recrystallization of A Grit-Blasted Single-Crystal Superalloy

Influence of Cooling Scenarios on the Evolution of Microstructures in Nickel-Based Single Crystal Superalloys

Experimental Investigation on Recrystallization Mechanism of a Ni-base Single Crystal Superalloy

Effect Of Strain On Recrystallization Of A Ni-Based Single Crystal Superalloy

Effect Of Re On Recrystallization Behavior Of Ni3al Based Single Crystal Alloy

Unveiling the Re effect on long-term coarsening behaviors of γ′ precipitates in Ni-based single crystal superalloys

Microstructure and Microsegregation in A Ni-Based Single Crystal Superalloy Directionally Solidified under High Thermal Gradient

Re Segregation at Interfacial Dislocation Network in a Nickel-Based Superalloy

Evolution of Static Recrystallization Microstructure Caused by Residual Strain of an Al-richen Ni-based Single Crystal Superalloy

Effect of Remelting Solution Heat Treatment on Microstructure Evolution of Nickel-Based Single Crystal Superalloy Dd5

Kinetics and microstructural evolution during recrystallization of a single crystal superalloy

Recrystallization and Inter-diffusion Behaviors of NiCrAlYSi Coating/DD6 Single Crystal Superalloy System

The Effects of Rhenium and High-Angle Grain Boundaries Upon the Elemental Distribution and Microstructure of Ni-Based Single-Crystal Superalloys

Recrystallization behavior of a high γ′-fraction Ni-based single crystal superalloy induced by residual strain

Influence of Heat Treatments on Incipient Melting Structures of DD5 Nickel-Based Single Crystal Superalloy