Abstract:This report describes a facile method for preparing mesoporous TiO2 microspheres (TMs) for scattering layer in DSSCs. In this method, TMs can be synthesized by direct hydrolysis of TiCl4 in ethanol aqueous solution at 40 degrees C, and the microspheres size could be easily controlled by varying the adding amount of CTAB. The TMs were characterized by scanning electron microcopy (SEM), X-ray diffraction (XRD), and nitrogen sorption analysis. A possible formation mechanism of the TMs was proposed on the basis of time-dependent measurements by TEM. Photoanodes consisting of the TMs as scattering layers were then fabricated. The use of TMs largely enhances the dye loading and gives highly effective light scattering. Using TMs with a diameter of 400 nm (TM400), a high photon to electricity conversion of 9.33% has been achieved, indicating a 24% increase in the conversion efficiency compared to the photoanode without scattering layer (7.54%). The charge transport behavior of the cells was investigated by intensity-modulated photocurrent and photovoltage spectroscopic analysis (IMPS and IMVS), and the results indicates that the DSSCs with TM400 as a scattering layer has a higher eta(cc) (80.2%) value than the DSSCs without a scattering layer (71%). This method provides a feasible way for fabricating low-cost scattering layers in DSSCs. (C) 2013 Elsevier Ltd. All rights reserved.

Synthesis of mesoporous TiO 2 spheres and aggregates by sol–gel method for dye-sensitized solar cells

Controlling Synthesis of Well-Crystallized Mesoporous TiO2 Microspheres with Ultrahigh Surface Area for High-Performance Dye-Sensitized Solar Cells

Monodisperse Mesoporous TiO2 Microspheres for Dye Sensitized Solar Cells

Synthesis of anatase TiO2 microspheres and their efficient performance in dye-sensitized solar cell

Size-controlled nanoporous TiO2 spheres with high dye-loading: Facile synthesis and application as scattering layers in dye-sensitized solar cells

Study on the Fabrication and Photovoltaic Property of TiO2 Mesoporous Microspheres

Single-Layer TiO2 Film Composed of Mesoporous Spheres for High-Efficiency and Stable Dye-Sensitized Solar Cells

Preparation of TiO2 spheres with hierarchical pores via grafting polymerization and sol–gel process for dye-sensitized solar cells

In Situ Synthesis of Mesoporous Tio2 Anatase Films and Their Photovoltaic Performance in Dye Sensitized Solar Cells

Macro-mesoporous TiO2 Microspheres for Highly Efficient Dye-Sensitized Solar Cells

Self-assembly and Photocatalysis of Mesoporous TiO 2 Nanocrystal Clusters

Mesoporous TiO2 Single-Crystal Polyhedron-Constructed Core–Shell Microspheres: Anisotropic Etching and Photovoltaic Property

Surfactant directed self-assembly of size-tunable mesoporous titanium dioxide microspheres and their application in quasi-solid state dye-sensitized solar cells

Synthesis and characterization of mesoporous TiO2 nanostructured films prepared by a modified sol–gel method for application in dye solar cells

Monodisperse Tio2 Hierarchical Hollow Spheres Assembled By Nanospindles For Dye-Sensitized Solar Cells

Synthesis and Formation Mechanism of Mesoporous TiO2 Microspheres for Scattering Layer in Dye-Sensitized Solar Cells

Rutile Tio2. Microspheres with Exposed Nano-Acicular Single Crystals for Dye-Sensitized Solar Cells

A Simple Solvothermal Process to Synthesize CaTiO3 Microspheres and Its Photocatalytic Properties

Interfacial Confined Formation Of Mesoporous Spherical Tio2 Nanostructures With Improved Photoelectric Conversion Efficiency

Preparation of Hierarchical TiO2 Microspheres for Enhancing Photocurrent of Dye Sensitized Solar Cells

Tunable synthesis of mesoporous titania with different morphologies for dye-sensitized solar cells