Infiltrated Ni 0.08 Co 0.02 CeO 2– x @Ni 0.8 Co 0.2 Catalysts for a Finger-Like Anode in Direct Methane-Fueled Solid Oxide Fuel Cells
Nai Shi,Yun Xie,Yi Yang,Daoming Huan,Yang Pan,Ranran Peng,Changrong Xia,Chusheng Chen,Zhongliang Zhan,Yalin Lu
DOI: https://doi.org/10.1021/acsami.0c17339
2021-01-25
Abstract:Direct utilization of methane in solid oxide fuel cells (SOFCs) is greatly impeded by the grievous carbon deposition and the much depressed catalytic activity. In this work, a promising anode, taking finger-like porous YSZ as the anode substrate and impregnated Ni<sub>0.08</sub>Co<sub>0.02</sub>Ce<sub>0.9</sub>O<sub>2−δ</sub>@Ni<sub>0.8</sub>Co<sub>0.2</sub>O as the novel catalyst, is fabricated via the phase conversion-combined tape-casting technique. This anode shows commendable mechanical strength and excellent catalytic activity and stability toward the methane conversion reactions, which is attributed to the exsolved alloy nanoparticles and the active oxygen species on the reduced Ni<sub>0.08</sub>Co<sub>0.02</sub>Ce<sub>0.9</sub>O<sub>2−δ</sub> catalyst as well as the facilitated methane transport rooting in the special open-pore microstructure of the anode substrate. Strikingly, this button cell delivers an excellent peak power density of 730 mW cm<sup>–2</sup> at 800 °C in 97% CH<sub>4</sub>/3% H<sub>2</sub>O fuel, only 9% lower than that in 97% H<sub>2</sub>/3% H<sub>2</sub>O. Our work shed new light on the SOFC anode developments.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.0c17339?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.0c17339</a>.Pore size distribution of the YSZ backbone, XRD results of NCCO and NCO, TPR profile of NCCO, XPS spectra of Ce 3d in NCCO and NC-CeO<sub>2–<i>x</i></sub>, TEM results of NCCO and NC-CeO<sub>2–<i>x</i></sub>, <i>I</i>–<i>V</i>–<i>P</i> plots, EIS and SEM results of button cells, and SVUV-PIMS results of methane conversions (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c17339/suppl_file/am0c17339_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology