Abstract:A nanoporous composite film combined of conducting inorganic template (TiO2/SnO2) and conducting polymer catalyst (poly(3,4-ethylenedioxythiophene):polystyrenesulfonate, PEDOT:PSS) was developed as an alternative counter electrode for dye-sensitized solar cell (DSSC) through low temperature process. The TiO2/SnO2 template was first fabricated by coating a homogeneous TiO2 nanoparticles. blended paste containing a SnCl4 aqueous solution on the conductive substrate, followed by annealing at 150 degrees C. The counter electrode was then completed by spin coating the PEDOT:PSS aqueous solution into the template and drying at 80 degrees C. The obtained TiO2/SnO2/PEDOT:PSS (TSP) composite film exhibits more excellent catalytic activity for the triiodide reduction than the pristine PEDOT:PSS film, resulting in the significant improvements in the fill factor and efficiency of the cells. The values of the fill factor and efficiency respectively increase from 0.564 and 4.79% to 0.699 and 6.54%. Noted that the photovoltaic performances of the TSP based DSSC is very similar to those of the Pt based one. The fill factor and efficiency of the later are 0.696 and 6.48%, respectively. The outstanding properties of the TSP composite film used as the counter electrode can be ascribed to its prominent synergistic effects. In the TSP composite film, the conducting TiO2 is applied as the main skeleton material with the in-situ formed SnO2 as a binder to construct a nanoporous structure for the PEDOT:PSS coating and also to provide numerous high-speed conductive paths for the electron transportation from the substrate to the PEDOT:PSS coating, and the PEDOT:PSS adhered on the TiO2/SnO2 skeleton mainly acts as the catalyst to enlarge its surface area allowing for more active sites for the tri-iodide reduction.

An Efficient Metal Conductor Paste/Nanoporous Carbon Composite Counter Electrode for Dye-Sensitized Solar Cells

A Low Cost Mesoporous Carbon/sno2/tio2 Nanocomposite Counter Electrode for Dye-Sensitized Solar Cells

Flexible counter electrodes with a composite carbon/metal nanowire/polymer structure for use in dye-sensitized solar cells

NiCo2O4/carbon nanofibers composite as an efficient counter electrode for dye-sensitized solar cells

Electrospinning Synthesis and Electrocatalytic Performance of Iron Oxide/carbon Nanofibers Composites As a Low-Cost Efficient Pt-free Counter Electrode for Dye-Sensitized Solar Cells

Low-cost Counter Electrodes Based on Nitrogen-Doped Porous Carbon Nanorods for Dye-Sensitized Solar Cells

Hierarchical porous nano-carbon composite: Effective fabrication and application in dye sensitized solar cells

An Efficient Dye-Sensitized Solar Cell Using Surfactant-Modified Mesoporous Carbon Film As a Counter Electrode

Enhancing photovoltaic performance in dye-sensitized solar cells using nanostructured NiS/MoS 2 composite counter electrodes

High performance platinum nanofibers with interconnecting structure using in dye-sensitized solar cells

Enhanced Electrocatalytic Performance of a Porous G-C3 N4 /graphene Composite As a Counter Electrode for Dye-Sensitized Solar Cells.

Enhanced Efficiency of Dye-Sensitized Solar Cells Based on Polymer-Assisted Dispersion of Platinum Nanoparticles/Carbon Nanotubes Nanohybrid Films as FTO-Free Counter Electrodes

Graphitic Carbon Nitride/multiwalled Carbon Nanotubes Composite As Pt-free Counter Electrode for High-Efficiency Dye-Sensitized Solar Cells

G-C 3 N 4 /conductive Carbon Black Composite As Pt-free Counter Electrode in Dye-Sensitized Solar Cells

Low-temperature preparation of graphite/activated carbon composite counter electrode and its photovoltaic performance and impedance characteristic

Low-Cost Snsx Counter Electrodes for Dye-Sensitized Solar Cells

In-situ Formation of Dispersed ZnO Nanoparticles in Mesoporous Carbon Counter Electrode for Efficient Dye-Sensitized Solar Cells

Nanoporous TiO2/SnO2/Poly(3,4-ethylene-dioxythiophene): Polystyrenesulfonate Composites As Efficient Counter Electrode for Dye-Sensitized Solar Cells

Flexible, metal-free composite counter electrodes for efficient fiber-shaped dye-sensitized solar cells

High-Efficiency Dye-Sensitized Solar Cells Based on Kesterite Cu 2 ZnSnSe 4 Inlaid on a Flexible Carbon Fabric Composite Counter Electrode

CoSe2/N-Doped Carbon Hybrid Derived from ZIF-67 As High-Efficiency Counter Electrode for Dye-Sensitized Solar Cells