Abstract:Owing to the excellent biocompatibility and corrosion-resistance of titanium and bioactivity of hydroxyapatite, the titanium/hydroxyapatite composite material combining their advantages is a highlight with bright prospects in medical clinics. In the present paper, the microarc oxidation (MAO) was performed on commercial pure titanium at first. Furthermore, the hydrothermal treatment (HT)was given with media of deionized water at 200°C for 4h in an autoclave. The surface morphology of the samples was observed by scanning electron microscopy (SEM), and the detailed composition was analyzed with Energy-Dispersive X-Ray Spectroscopy (EDS). The X-ray diffraction analysis (XRD) was employed to characterize the crystal structure of composite. The results indicate that the titania film contains the Ca and P elements on titanium substrate after MAO, which converts into the hydroxyapatite crystals via hydrothermal treatment. The smaller size and amount of hydroxyapatite crystals are found when lower voltage is presented. But there are converse phenomena with higher voltage, especially, the differences can be neglected above 400V. It is shown that the micro-hole and hollow surface of titania film can induce the hydroxyapatite nucleation and growth as two different forming ways. The hydroxyapatite has a preference of forming in hollow surface with lower voltage, however, the presences of the micro-hole and hollow surface of titania film are occurring for higher voltage. The hydroxyapatite forming in micro-hole shows needle-like crystal and high bonding strength with surrounding titania film because of the mechanical restrict force from micro-hole wall. Also it is noted that hydroxyapatite crystals incline to precipitate on the film surface with high Ca and P concentrations after the hydrothermal treatment.

Biocompatibility Research of Medicine Titanium Alloy Coating by Microarc Oxidation

Review of the Biocompatibility of Micro-Arc Oxidation Coated Titanium Alloys

Biocompatibility of HAP/Ti Gradient Coating by Microarc Oxidation and Biomimetic Process

Investigation on Biocompatibility of Micro-arc Oxidation Ti6Al4V Alloy

Preparation of Bio-film on the Surface of Titanium Alloy by Micro-arc Oxidation and Hydro-thermal Synthesis and Its Histocompatibility

Studies on the Bioceramic Coating on Titamium Substrate Including Silicon and Calcium by Micro-Arc Oxidation and Osteoblast’s Adhesion and Proliferation on the Coating

Hydroxyapatite formation of Ca and P modified micro-arc oxidation coating on Ti alloy

Review of Microarc Oxidation of Titanium Implant

Fracture Mechanics Study on Porosity Zirnocia/hydroxyapatite Coating Obtained through Microarc Oxidation on Medical Titanium Alloy Surface

Effect of Micro-Arc Oxidation on Antimicrobial Properties and Biocompatibility of Biomedical Ti-xFe Alloys

Effect of Electrolyte Composition on the Microstructure and Bio-Corrosion Behavior of Micro-Arc Oxidized Coatings on Biomedical Ti6Al4V Alloy

Hydroxyapatite coatings produced on commercially pure titanium by micro-arc oxidation.

Structure and composition of titania films with different chemical composition on the surface of titanium implant by microarc oxidation

Effect on osteoblast adhesion and bone implants behavior of the titanium treated with microarc oxidation and alkali

Preparation of TiO2/HA composite coating by micro-arc oxidation on titanium surface

Titanium based hydroxyapatite/chitosan coating prepared by microarc oxidation process and its biological characteristics

Microstructure and Corrosion Behavior of Coated AZ91 Alloy by Microarc Oxidation for Biomedical Application

Biological and antibacterial properties of the micro-nanostructured hydroxyapatite/chitosan coating on titanium

Influence of Hydrothermal Treatment in Deionized Water on Surface Morphology and Structure of Titanium with Biomedical Application by Microarc Oxidation

Preparation of Biocompatible Structural Gradient Coatings on Pure Titanium

The Biocompatibility of Hydroxyapatite Film Deposition on Micro-Arc Oxidation Ti6Al4V Alloy