Abstract:Developing formaldehyde-free and excellent water resistance has constantly been at the center of attention of wood adhesives. In addition to enhancing the adhesive itself, the modification of wood interface can also improve its bonding strength and water resistance. In this study, aqueous solutions of NaIO 4 and NaClO 2 have been sprayed onto the surface of poplar veneer evenly. An activated wood interface equipped with -CHO and -COOH was prepared. Traditional polyurethane adhesives are primarily two-component, with excessive manufacturing cost, complicated production and use procedures. In this study, a single component high branched polyurethane adhesive (GI) was synthesized via a A 2 +B 3 oligomerization method by using glycerol and isophorone diisocyanate (IPDI). Using branched polyamine (PA 4 N ) as a modifier, GI was modified to GI-PA 4 N , which was used as an adhesive and then hot pressed with the activated wood to make three-layer plywood. The bonding interface was equipped with urethane bonds, urea-based chemical bonds, amide bonds, Schiff bonds and hydrogen bond, which considerably enhanced the stability and water resistance of the bonding interface. FT-IR and XPS confirmed the existence of -CHO and -COOH at the interface of the activated wood, and characterized the synthesis mechanism and bonding mechanism of GI-PA 4 N . The results indicated that when the mass ratio of polyurethane to polyamine was 4:1, the overall performance of the adhesive was the best. The dry bonding strength increased from 1.92 MPa to 3.63 MPa, and the wet bonding strength increased from 1.77 MPa to 3.13 MPa, much higher than the minimum requirement of GB/T 17657–2013 (0.7 MPa). A formaldehyde-free, high-performance plywood with excellent water resistance was successfully prepared using wood interfacial activation and branched polyamine modification.

Preparation and Characterization of Silicate Wood Adhesive Modified with Ammonium Stearate

MALDI ToF Investigation of the Reaction of Soy Protein Isolate with Glutaraldehyde for Wood Adhesives

Preparation and properties of isocyanate prepolymer/corn starch adhesive

Preparation, characterization and properties of an organic siloxane-modified cassava starch-based wood adhesive

Preparation of isocyanate virtual 'core-shell' and its application in wood adhesive

Effectiveness of Surface Treatment on Bonding Performance of Starch-Based Aqueous Polymer Isocyanate Wood Adhesive

Preparation of Polyacrylate Emulsion with High Adhesion Properties by Adding Modified Silica Sol

Preparation and characterization of the bonding performance of a starch-based water resistance adhesive by Schiff base reaction

Easy Preparation, High Water Resistance Glucose-Based Environment-Friendly Wood Adhesives

Bonding properties of polyurethan enhanced by branched polyamine and wood interfacial activation

Study on the Effect of Acrylic Acid Emulsion on the Properties of Poplar Wood Modified by Sodium Silicate Impregnation

Preparation of starch polyols adhesive

Preparation and characterization on the eco-friendly corn starch based adhesive of with salient water resistance, mildew resistance

Preparation Of Nanosilica Reinforced Waterborne Silylated Polyether Adhesive With High Shear Strength

Preparation, Characterization and Properties of Starch-Based Wood Adhesive

An Environmentally Friendly and High Wet-Bond Strength Adhesive Based on Starch, Itaconic Acid and Silicone

Environmentally friendly chitosan adhesives for plywood bonding

Silane Modification of Starch-Based Wood Adhesive: Review

Modified phenol formaldehyde resin with sodium silicate as a low-cure wood adhesive

Developing High-Performance Cellulose-Based Wood Adhesive with a Cross-Linked Network

Bioinspired water-retaining and strong soybean flour-based adhesive for efficient preparation of plywood