Abstract:To study the effect of thermal cold cycling on the microstructure and properties of Al–Cu–Mg–Ag alloy, hardness and tensile tests, resistivity tests, friction and wear tests, intergranular corrosion, and electrochemical corrosion tests were used to explore its mechanical properties, wear resistance, and corrosion resistance changes. Laser confocal microscopy, scanning electron microscopy, optical microscopy, and transmission electron microscopy were used to observe and analyze the wear morphology, corrosion conditions, and microstructure of the alloy. The results show that after thermal cold cycling, the phase of the Al–Cu–Mg–Ag alloy is a fine and dense Ω phase, and the microstructure is significantly optimized, effectively improving the properties of the alloy. As the number of cycles increases, the properties of the alloy change accordingly, when thermal cold cycled twice (TCC2), the small Ω phase is dispersed and evenly distributed on the matrix, which enhances the strengthening effect of the alloy. The hardness, yield strength, and tensile strength of the alloy are 155.6 HV, 445 MPa, and 484 MPa, respectively. The conductivity and resistivity at this time are 55.2 %IACS and 31.1 nΩ m, respectively. The wear resistance of the alloy is also improved, and the wear depth is decreased. The average friction coefficient is 1.214, and the wear rate is 0.51 × 10 −4 mm 3 /m. The intergranular corrosion depth is 45 μm, the self-corrosion current density is 0.0048 mA cm −2 , corrosion weight loss is 8.3 mg/cm 2 , the passivation film thickness is 1.82 nm, and the corrosion resistance is higher. As the number of cycles continues to increase, the aging time continues to extend, causing the size of the matrix precipitate phase to become coarser, the strengthening effect is weakened, and the properties of the corresponding alloy become degenerate.

Effect of Cycle Index on the Microstructural Evolution of Alumina Particles Reinforced Aluminum Composites Treated by Cryogenic Treatment

The Influence of Cryogenic Treatment on the Microstructure and Mechanical Characteristics of Aluminum Silicon Carbide Matrix Composites

Influence of Cooling Speed on the Microstructure of Particles Reinforced 7055al Composites Subject to Regulatory Cryogenic Treatment

Effect of Cryogenic Pre-Treatment on Aging Behavior of In-Situ TiB2/Al–Cu–Mg Composites

Effects of Cryogenic Treatment on Mechanical Properties of SiCp/A356 Composites

Effect of thermal-cooling cycle treatment on thermal expansion behavior of particulate reinforced aluminum matrix composites

Effect of Pretreatment and Cryogenic Temperatures on Mechanical Properties and Microstructure of Al-Cu-Li Alloy

Effect of deep cryogenic treatment on the microstructure and mechanical properties of Al–Cu–Mg–Ag alloy

Effect of Thermal Cycling Treatment on Microstructure and Mechanical Properties of AlNp/2024A1 Composite

Effect of Thermal Cycling Treatment on Microyield Behavior of Al 2 O 3 p/Al Composite

Influence of Cryogenic Treatment on Thermal Expansion Properties of SiCp/Al Composites

Effect of Deep Cryogenic Treatment on the Artificial Aging Behavior of 6082 Aluminum Alloy

Effect of thermal cycling on the mechanical properties of Cf/Al composites

Effect of Carbon Nanotubes and High Temperature Extrusion on the Microstructure Evolution of Al-Cu Alloy

Effect of Different Dimensional Stability Treatments on Microstructure and Mechanical Properties of SiC_p/2024Al Composite

Microstructural evolution and mechanical property of Cu‐Cr‐Zr‐ZrB2 composites subjected to cryorolling and aging treatment

Effect of deep cryogenic treatment on microstructures and mechanical properties of automotive 6063Al alloy

Effect of Cryogenic Treatment on Residual Stress and Microstructure of 6061 Aluminum Alloy and Optimization of Parameters

Effect of Deep Cryogenic Treatment on the Artificial Ageing Behavior of SiCp–AA2009 Composite

Influence of TiC particle size on microstructural evolution and fracture mechanism of TiC/Al-Cu composites

Effect of Thermal Cold Cycling on the Microstructure and Properties of Al–Cu–Mg–Ag Alloy