Synthesis of Thiol-Functionalized Mesoporous Calcium Silicate and Its Adsorption Characteristics for Heavy Metal Ions
Lihua Liu,Tong Li,Ganggang Yang,Yifeng Wang,Anping Tang,Yulin Ling
DOI: https://doi.org/10.1016/j.jece.2017.11.046
IF: 7.7
2017-01-01
Journal of Environmental Chemical Engineering
Abstract:Thiol-functionalized mesoporous calcium silicate (MCS-SH) was synthesized using post-grafting with calcium nitrate tetrahydrate and sodium metasilicate nonahydrate as raw materials, cetyl trimethyl ammonium bromide as template, and (3-mercaptopropyl) trimethoxysilane as modifying agent. The structure and composition were characterized using X-ray diffraction, Fourier-transform infrared spectroscopy, Brunauer-Emmett-Teller surface analysis, thermogravimetry-differential thermal analysis, scanning electron microscopy, transmission electron microscopy, and energy-dispersive X-ray spectrometry. The adsorption performance and thermodynamic and kinetic characteristics of MCS-SH for Cd2+, Cu2+, Pb2+, and Cr3+ were investigated. Results showed that MCS-SH possessed a slit-pore structure with a specific surface area of 129.32 m(2) g(-1) and pore size that was mainly distributed in 5-49 nm, which reduced by 28.81 m(2) g(-1) and 2 nm compared with those of unmodified mesoporous calcium silicate (MCS), respectively. The amount of -SH grafted to MCS-SH was 0.4594 mmol g(-1), according to the determined sulfur content. The maximum adsorption capacities for Cd2+, Cu2+, Pb2+, and Cr3+ were 601.51, 509.56, 618.09, and 334.81 mg g(-1) at 293 K, respectively, which were much higher than those reported in the literature, and follow the order of Pb2+ > Cd2+ > Cu2+ > Cr3+. The equilibrium data of the four heavy metal ions adsorbed by MCS-SH fitted the Langmuir model and, especially, the Redlich-Peterson model well. The adsorption processes were all endothermic, entropy increasing, and spontaneous. The adsorption of MCS-SH for Cd2+, Cu2+, Pb2+, and Cr3+ was rapid and attained equilibrium within 60 min. The adsorption kinetics can be well fitted by the pseudo-second-order model, and the adsorption activation energy followed the order of Cr3+ (29.7526 kJ mol(-1)) > Pb2+ (21.5840 kJ mol(-1)) > Cu2+ (19.6988 kJ mol(-1)) > Cd2+ (18.5377 kJ mol(-1)). The adsorption mechanisms include physical adsorption, chemical adsorption (especially surface complexing adsorption), and ion exchange, with chemical adsorption being the dominant mechanism. MCS-SH exhibited an excellent performance as adsorption material for Cd2+, Cu2+, Pb2+, and Cr3+.