Effect of heavy-doping Eu3+ and charge compensation on crystalline phase and luminescence properties of K2CaP2O7 phosphors emitting orange-red light
Yu-Huan Wang,Yong-Jie Chen,Xiu-Juan Geng,Ying Yang,Zi-Qing Li,Xiu-Yuan Zuo,Chen, Yong-Jie,Zuo, Xiu-Yuan
DOI: https://doi.org/10.1007/s12039-024-02251-z
2024-02-29
Journal of Chemical Sciences
Abstract:A series of K 2 Ca 1- x P 2 O 7 : x Eu 3+ phosphors were prepared by a high-temperature solid-state reaction method. The crystal structure was analyzed by X-ray diffraction (XRD). Fluorescence spectra, decay curves, and color coordinates were investigated. Under excitation at 393 nm, the strongest emission peak was located at 590 nm, corresponding to the 5 D 0 → 7 F 1 transition of Eu 3+ , and the sub-strongest one was located at 612 nm which belongs to the 5 D 0 → 7 F 2 transition of Eu 3+ . XRD results show that the patterns doped with a small amount of Eu 3+ were fitted well with the standard card of K 2 CaP 2 O 7 , while the pattern with the doping of high concentration Eu 3+ (heavy-doping) indicated the co-existence of K 2 CaP 2 O 7 and EuPO 4 phase which leads to luminescent intensity of phosphors enhance remarkablely. The concentration quenching mechanism was explained through dipole-dipole interaction. Different doping amounts of Eu 3+ and charge compensators will affect the symmetry of the host lattice, thereby affecting the emission intensity ratio of orange and red light. The color coordinates of K 2 Ca 0.49 P 2 O 7 :0.51Eu 3+ and K 2 Ca 0.33 P 2 O 7 :0.67Eu 3+ , 0.1Na + phosphor were near the red region, which was close to commercial red-emitting phosphors Y 2 O 3 :Eu 3+ and standard red light, respectively.
chemistry, multidisciplinary