Abstract:Without use of any templates or shape-protectors, uniformly sized anatase TiO2 nanocrystallites with cuboidal morphology were synthesized by changing titanium hydroxide precipitates into their corresponding ethanol-gels (viz. by washing several times with anhydrous ethanol) followed by drying in supercritical ethanol (7.0MPa, 270°C) and calcination at high temperature (AS-preparation). Characterizations with X-ray diffraction (XRD), Raman spectroscopy and nitrogen adsorption suggest that the cuboidal anatase nanocrystallites are highly resistant to thermal sintering. The anatase structure of the cuboidal nanocrystallites was maintained even after calcinations up to temperatures as high as 800°C. Thermogravimetric (TG) measurements in flowing air show that the as-prepared cuboidal TiO2 nanocrystallites were contaminated with some carbonaceous residues, which can be completely removed by calcination at 500°C in air. Application of these cuboidal TiO2 nanocrystallites as photocatalytic materials was evaluated by photocatalytic degradation of methyl orange in water. With increasing the calcination temperature up to 800°C, the photocatalytic activities of anatase TiO2 cuboids increased gradually due to improved crystallization of the material. The sample calcined at 800°C afforded the highest photocatalytic activity, which is comparable to that of the commercial photocatalyst Degussa P-25. Due to the presence of carbonaceous residues after the supercritical drying in the preparation, the samples calcined at temperatures no higher than 400°C showed higher photocatalytic activities than the sample calcined at 500°C. However, further calcination of the sample at 1000°C led to drastic reduction in the photocatalytic activity due to the anatase-to-rutile phase transformation and sintering of the material.

Nanometer Anatase Titania Synthesis by Reverse Titration Method and Evaluation of Their Photocatalytic Activity

Controllable Hydrothermal Synthesis, Optical and Photocatalytic Properties of TiO2 Nanostructures

Preparation and Photocatalytic Activities of TiO2 Nanotubes with Mixed Crystal Structure

Titania Nanoflowers with High Photocatalytic Activity

Fabrication and Photocatalytic Activity of Tio2 Nanofiber Membrane

Preparation and Photocatalytic Activity of TiO<sub>2</sub>/Fe<sub>2</sub>O<sub>3 &Lt;/sub>nanocomposite

Synthesis and photocatalytic properties of nano bi-crystalline titania of anatase and brookite by hydrolyzing TiOCl2 aqueous solution at low temperatures

Anatase-TiO2 nano-particle preparation with a micro-mixing technique and its photocatalytic performance

Preparation of TiO_2 Nanoparticle and Their Photocatalytic Property

Large-Scale Preparation Of Ordered Titania Nanorods With Enhanced Photocatalytic Activity

Preparation and Characterization of Nanosized Anatase TiO2 Cuboids for Photocatalysis

Characterization and photocatalytic activity of Ni-doped tiO2 nano photocatalysts prepared by low temperature combustion synthesis]

Preparation of Anatase-Type TiO_2 Nanoparticals from Ti (SO4)2 Solution under Hydrothermal Conditions and Its Photocatalytic Performance

Room‐Temperature Hydrolysis of Potassium Titanyl Oxalate and Water‐Assisted Crystallization for TiO2 with High Photocatalytic Activity

Preparation of Nanoparticle WO_3-doped TiO_2 and Research on Its Photocatalytic Activity

Direct Continuous Hydrothermal Synthesis of High Surface Area Nanosized Titania

PREPARATION OF IRON-DOPED TITANIA NANOCRYSTALLINE GRAINS AND ITS PHOTOCATALYTIC PROPERTY

Hydrothermal Preparation and Photocatalytic Properties of Quantum Size TiO2 Nanoparticles

Titanium dioxide (TiO2) Nanoparticles XRD Analyses: An Insight

Synthesis and Properties of Nano-Rutile Tio2 Photocatalysts

Highly Active Rutile TiO 2 for Photocatalysis