Abstract:Based on our previously proposed three-phase solidification model, a comprehensive analysis on the impact of the only electromagnetic stirring (EMS) and combined EMS on the microscopic structure evolution and solute segregation behavior in a 500 mm diameter 42CrMo steel of continuously cast round bloom. The results indicate that M-EMS has a notable impact on expediting the dissipation of superheat, enhancing the initiation of grain formation, and enlarging the equiaxed region. The percentage of equiaxed grains increased from 59.26 to 63.37% with the increment in current intensities of M-EMS from 250 to 350 A. However, higher M-EMS current intensities were found to enhance local positive segregation in the transition zone between columnar and equiaxed grains. The impact of M-EMS on improving center positive segregation was minimal, as the ratio of center positive segregation remained consistently around 1.17. Furthermore, the implementation of F-EMS demonstrated its effectiveness in reducing center positive segregation. The ratio of center positive segregation decreased from 1.14 to 1.10, when the current intensity increases from 150 to 250 A. However, it should be noted that F-EMS alone did not contribute to the expansion of the equiaxed zone. On the other hand, when M-EMS was combined with F-EMS (referred to as combined EMS), it showed potential in mitigating center segregation during continuous casting round blooms. The benefits observed with M-EMS in terms of promoting grain nucleation and expanding the equiaxed grain zone were also evident in this combined EMS process. Furthermore, a notable enhancement in the equiaxed grain ratio up to 60.13% was observed combined EMS models were simultaneously employed during continuous casting of round blooms. And, there was a reduction in center segregation ratio for round blooms to as low as 1.09.

Reduction in Macrosegregation on 380 Mm×490 Mm Bloom Caster Equipped Combination M+F-EMS by Optimising Casting Speed

Numerical Modeling of the Macrosegregation Improvement in Continuous Casting Blooms by Using F-EMS

Numerical investigation on effect of electromagnetic stirring on macrosegregation in continuously cast round bloom via three-phase solidification model

Effect of Mold Electromagnetic Stirring and Final Electromagnetic Stirring on the Solidification Structure and Macrosegregation in Bloom Continuous Casting

Control of macrosegregation at the steel gradient transition by submerged entry nozzle and mold electromagnetic stirring

Numerical simulation of coupled fluid flow and solidification in a curved round bloom continuous caster with a combined rotary electromagnetic stirring

Effect of M-EMS current intensity on the subsurface segregation and internal solidification structure for bloom casting of 42CrMo steel

Improvement of carbon segregation in billet by final-EMS, based on segmented continuous casting model

High-efficiency continuous casting of GCr15 bearing steel bloom based on cooperative control technique of complex electromagnetic stirring and soft reduction

Three-Dimensional Macrosegregation Model of Bloom in Curved Continuous Casting Process

Numerical Simulation of Fluid Flow, Solidification, and Solute Distribution in Billets under Combined Mold and Final Electromagnetic Stirring

Numerical simulation of macrosegregation in billet continuous casting influenced by electromagnetic stirring

Numerical Simulation of Macrosegregation in Continuously Cast Slab with Application of S-EMS and MR

Improving compositional homogeneity of CF53 steel products by modifying their solidification structure and F-EMS intensity

Improving Inner Quality in Continuous Casting Rectangular Billets: Comparison Between Mechanical Soft Reduction and Final Electromagnetic Stirring

Effect of Electromagnetic Stirring on Solidification Structure and Central Porosity of Large‐Sized Round Bloom in Continuous Casting

Numerical and Experimental Study on Carbon Segregation in Shaped Billet of Medium Carbon Steel with Combined Electromagnetic Stirring.

Study on the synergistic effect of electromagnetic stirring and mechanical reduction on the improvement of the internal homogeneity of high-carbon steel billet

Modeling of the as-cast structure and macrosegregation in the continuous casting of a steel billet: Effect of M-EMS

Effect of Electromagnetic Stirrer Position on Mold Metallurgical Behavior in a Continuously Cast Bloom

Effect of Mold Electromagnetic Stirring Position on Flow Field and Solidification Behavior of Four‐Hole Nozzle Arc Continuous Casting Large Round Bloom