Simple Strategy for Synthesizing LiNi 0.8 Co 0.15 Al 0.05 O 2 Using CoAl-LDH Nanosheet-Coated Ni(OH) 2 as the Precursor: Dual Effects of the Buffer Layer and Synergistic Diffusion
Peng Xiao,Yu Cao,Wenhao Li,Gang Li,Yongli Yu,Zhongjia Dai,ZeXue Du,Xu Chen,Jie Sun,Wensheng Yang
DOI: https://doi.org/10.1021/acsami.1c07551
2021-06-21
Abstract:Ni-rich layered oxide LiNi<sub>0.8</sub>Co<sub>0.15</sub>Al<sub>0.05</sub>O<sub>2</sub> is a promising cathode material for high-power lithium-ion batteries due to its high energy density and low cost. However, obtaining LiNi<sub>0.8</sub>Co<sub>0.15</sub>Al<sub>0.05</sub>O<sub>2</sub> with a large and uniform particle size and without undesired Al-related phases using some conventional synthesis methods is quite difficult. These problems seriously affect the electrochemical performance of LiNi<sub>0.8</sub>Co<sub>0.15</sub>Al<sub>0.05</sub>O<sub>2</sub>, thus impeding its wide application. Here, we propose a simple strategy to synthesize LiNi<sub>0.8</sub>Co<sub>0.15</sub>Al<sub>0.05</sub>O<sub>2</sub> using CoAl-layered double hydroxide (CoAl-LDH) nanosheet-coated Ni(OH)<sub>2</sub> as the precursor. Compared with LiNi<sub>0.8</sub>Co<sub>0.15</sub>Al<sub>0.05</sub>O<sub>2</sub> synthesized from nickel-cobalt-aluminum hydroxide and Al(OH)<sub>3</sub>-coated nickel-cobalt hydroxide precursors, LiNi<sub>0.8</sub>Co<sub>0.15</sub>Al<sub>0.05</sub>O<sub>2</sub> produced using the proposed approach showed good sphericity, a large and uniform particle size, a pure phase, and excellent electrochemical performance. The superior properties are attributed to the dual effects of the buffer layer and synergistic diffusion. Specifically, the CoAl-LDH coating layer reacts with LiOH during the lithiation-calcination process to form a Li<sub>1-<i>x</i></sub>(Co<sub>0.75</sub>Al<sub>0.25</sub>)<sub>1+<i>x</i></sub>O<sub>2</sub> mesophase as the buffer layer, which increases the formation temperature of the layered structure and reduces Li<sup>+</sup>/Ni<sup>2+</sup> cation mixing, making a well-ordered crystal structure. Moreover, spectroscopic analysis results and density functional theory calculations indicated a synergistic diffusion effect between Co and Al, and the presence of Co on the surface promotes the diffusion of Al during the lithiation-calcination process, thus avoiding the formation of undesired Al-related phases and allowing for a uniform element distribution.
materials science, multidisciplinary,nanoscience & nanotechnology