Abstract:The mixed matrix membranes (MMMs) were prepared from crosslinked PDMS incorporated with HF acid etched ZSM-5. ZSM-5 zeolite was etched with a series of HF aqueous-acetone solution and characterized by SEM, BET, XRD and FT-IR. It was found that HF etching process was very effective for removing organic impurities in zeolite and micro-pores were observed out of the surface of zeolite particles, which enhanced the hydrophobicity and surface roughness of ZSM-5 successfully. Both tensile strength and swelling resistance of ZSM-5/PDMS MMMs increased with the rising concentration of HF solution, which can mainly be attributed to the improved zeolite-PDMS interfacial adhesion resulted from the intrusion of PDMS into micro-pores out of the ZSM-5 surface. Subsequently, the sorption experiment was performed with the results suggesting preferential sorption of ethanol by MMMs. Moreover, the sorption selectivity of ZSM-5/PDMS MMMs increased notably as the concentration of HF solution increased. The pervaporation performance of ethanol/water mixtures using MMMs was also investigated in detail. The MMMs filled with etched ZSM-5 showed much better selectivity than that filled with non-etched ones, with a little expense of permeability. It was found that with the same zeolite loading, increasing the HF acid concentration in etching process enhanced the zeolite-PDMS interfacial adhesion which promoted the ethanol selectivity of MMMs, while depressed the total permeation flux a little. In addition, both ethanol permeation and the selectivity increased with an increase of the zeolite loading from 10% to 30%. Nevertheless, excessive zeolite loading or decreasing thickness of selective layer led to the poor selectivity to ethanol. A decline of the ethanol selectivity was also observed as the feed ethanol concentration as well as feed temperature increased.

Poly(vinyl Alcohol)/zif‐8‐nh2 Mixed Matrix Membranes for Ethanol Dehydration Via Pervaporation

A high ZIF-8 loading PVA mixed matrix membrane on alumina hollow fiber with enhanced ethanol dehydration

Comprehensive Analysis on Anomalous Phenomenon of Ethanol-Soluble PVB Membrane for Ethanol Recovery Via Pervaporation

Incorporating Mixed-Ligand Zeolitic Imidazolate Framework into Polydimethyldiethoxysilane (PDMDES) Membrane for Enhancing Alcohol Pervaporation Recovery.

Synthesis and characterization of high-flux ZIF-90/poly-dimethyldiethoxysilane (PDMDES) mixed matrix membrane for enhanced pervaporation recovery of alcohols

Enhanced Ethanol Recovery of PDMS Mixed Matrix Membranes with Hydrophobically Modified ZIF-90

ZIF-90/P84 mixed matrix membranes for pervaporation dehydration of isopropanol

(3-Aminopropyl) Triethoxysilane-Modified ZIF-90 Nanoparticle/Polydimethylsiloxane Mixed Matrix Membranes for Ethanol Recovery via Pervaporation

Silane-modified NaA/PAAs hybrid membranes for ethanol dehydration by pervaporation

Asymmetric poly (vinyl alcohol)/Schiff base network framework hybrid pervaporation membranes for ethanol dehydration

Pervaporative poly(vinyl alcohol)/H‐β zeolite mixed matrix membranes for dewatering C2–C3 alcohols

Facile Preparation of Thin and Nanodisperse ZIF-8/PDMDES Hybrid Membrane for Efficient Alcohol Recovery Via Pervaporation

Facile Covalent Crosslinking of Zeolitic Imidazolate Framework/Polydimethylsiloxane Mixed Matrix Membrane for Enhanced Ethanol/Water Separation Performance

ZIF-8@GO Composites Incorporated Polydimethylsiloxane Membrane with Prominent Separation Performance for Ethanol Recovery

Mixed matrix membranes with HF acid etched ZSM-5 for ethanol/water separation: Preparation and pervaporation performance

Three‐component Mixed Matrix Organic/inorganic Hybrid Membranes for Pervaporation Separation of Ethanol–water Mixture

A Novel Modified ZIF-8 Nanoparticle with Enhanced Interfacial Compatibility and Pervaporation Performance in a Mixed Matrix Membrane for De-Alcoholization in Low-Concentration Solutions

ZIF-7/PDMS Mixed Matrix Membranes for Pervaporation Recovery of Butanol from Aqueous Solution

Silane-Modified Naa Zeolite/Paas Hybrid Pervaporation Membranes for the Dehydration of Ethanol

Zif-8 Filled Polydimethylsiloxane Membranes for Pervaporative Separation of N-Butanol from Aqueous Solution

Improved Ethanol Recovery Through Mixed-Matrix Membrane with Hydrophobic Maf-6 As Filler