Controllable Synthesis and Electrocatalytic Activity of Hierarchical Pd-based Nano-catalysts for DFAFCs
Zhengyu Bai,Shujun Chao,Lu Niu,Min Shi,Lin Yang
2014-01-01
Abstract:Noble metal nanomaterials with hierarchical structures are considered to be promising catalysts owing to its controlling crystal morphology, good chemical stability and environmental-friendly. In order to improve the electrocatalytic activity of catalysts and maximize the utilization of nobel metal, Pd-based catalysts with hierarchically structures were successfully synthesized in the presence of different organic additives at ordinary temperature . And the influence of the c omponent and morphology on the electrocatalytic properties of catalysts was also studied. Firstly, a series of Pd hollow nanosphere s and nanopaticles with different particle size were prepared in the presence of conducting polymers or different organic additives. Compared with the solid nanoparticles, Pd hollow nanospheres show a very high electrochemically-active surface area and significant increase in electrocatalytic activity ( 1 60 mA cm -2 ) towards formic acid oxidation, which make them the preferable catalysts for direct formic acid fuel cells (DFAFC). Secondly, a series of Pd-based (PdCu, PdCo, PdRh et al.) bimetal lic alloyed hollow nanosphere s composed with nanopaticles were successfully synthesized by a novel one-pot template-free strategy . According to cyclic voltammograms , t he maximal peak current density of hollow PdCu alloyed nanocubes is 190 mA cm -2 , greater than those of PdCu alloy catalyst (143.1 mA cm -2 ) and Pd nanopaticles (106.8 mA cm -2 ). The results reveal that the alloy hollow nanostructures have high electrochemical activity , good stability and excellent anti-CO toxic ability during the process of formic acid oxidation . A t the same time, it is one of the effective approaches to reduce the loading of noble metals and lower the cost of the catalysts . Thirdly, a series of Pd- MeO x (Pd -Fe 2 O 3 , Pd -CeO 2 , Pd -SnO 2 et al.) hybrid nanostructured electro catalysts were successfully prepared in the presence of different organic additives at ordinary temperature . On the surface of such metal oxides, hydroxyl species ( OH - ) could form easily and assist oxidization of the adsorbed intermediate species during the electrooxidation. In short, the Pd- MeO x catalyst not only lowers the cost by means of less Pd dosage but also shows good performance for electrooxidation with the assistance of oxide additives. Overall, the c omponent and morphology are key factors to the excellent performance of the catalysts . The results reveal that h ollow nanos tructures composed with nanopaticles represent a new class of powerful catalysts because of the increased surface area, low density and surface permeability . As a result, the catalyst with b imetallic alloy is an effective approach to enhance the catalytic activity, and reduce the cost of catalysts. Obviously, design and synthesis of hollow bimetallic nanosphere catalysts represent a promising way to effectively improve the performance and utilization of catalysts, while the cost can be further decreased .