Abstract:Silver nanowires (AgNWs) have attractive applications in the fabrication of flexible electronics because of their adequate electrical conductivity, mechanical properties, and oxidation resistance. However, the film produced by AgNW ink needs to be sintered at temperatures above 200 °C to obtain high electrical conductivity, which is incompatible with commonly used flexible substrates such as paper or polymer materials. In this study, the AgNW network was decorated by in situ reduced Ag particles (AgPs) to improve the structural integrity and conductivity of the film. After sintering at 80 °C, the pores and voids within the AgNW network were filled with Ag particles smaller than 200 nm, and the porosity of the film was markedly reduced. The lowest resistivity value was 3.9×10-5 Ω•cm after sintering at 100 °C, only 10.8% and 8.5% of the resistivity values of the films produced from AgNW and ion inks, respectively. During sintering, Ag nucleated on the surface of AgNWs, and its growth and agglomeration resulted in interconnections between the AgNWs and Ag particles. Thereafter, the bridging and filling effect of the Ag particles facilitated the formation of a compact and firm network, improving the film conductivity. The line film printed from the composite ink with 10 layers exhibited a low resistivity of 7.3×10-7 Ω•m. Even after 5000 bending cycles, the resistivity of the line only increased by 4.47×10-6 Ω•cm from the initial value. The composite ink reported in this study is a promising candidate for the low-cost printing of ultralow-power-consumption wearable electronic devices.

Synthesis and characterization of Ag nanorods used for formulating high-performance conducting silver ink

Facile Synthesis of Silver Nanoparticles and Preparation of Conductive Ink

Preparation of Nano-Silver Conductive Ink and Electrode Properties

Direct pen writing and atomic-scale molecular dynamics simulation study of a novel silver nano-ink

Green Approach to Prepare Silver Nanoink with Potentially High Conductivity for Printed Electronics

Synthesis and Characterizing of High Aspect Ratio Silver Nanowires by Polyol Process

Highly Conductive Ink Made of Silver Nanopolyhedrons Through an Ecofriendly Solution Process

Preparation of silver nanoparticles and application in water-based conductive inks

One-step Synthesis of Ag Nanoparticles for Fabricating Highly Conductive Patterns Using Infrared Sintering

Electrical conductivity of silver conductive ink synthesized using chemical reduction method

Preparation, Characterization and Reaction Mechanism of A Novel Silver-Organic Conductive Ink

Green Synthesis of Silver Nanoparticles with Glucose for Conductivity Enhancement of Conductive Ink

One-pot Rapid Synthesis of High Aspect Ratio Silver Nanowires for Transparent Conductive Electrodes

Conductivity enhancement of Ag nanowire ink by decorating in situ formed Ag particles under low-temperature sintering

Preparation of Silver Nanorods by Electrochemical Methods

Preparation of low-temperature sintered high conductivity inks based on nanosilver self-assembled on surface of graphene

Green synthesis of dendritic silver nanostructure and its application in conductive ink

Cost-effective Silver Nano-Ink for Inkjet Printing in Application of Flexible Electronic Devices

Synthesis, characterization and self-assembly of silver nanowires

Preparation, structure and properties of high performance silver-filled UV-curable polyurethane acrylate conductive inks

Fabrication, characterization and screen printing of conductive ink based on carbon@Ag core-shell nanoparticles