Abstract:A one-step sintering process was developed to produce magnetocaloric La(Fe,Si)13/Ce-Co composites. The effects of Ce2Co7 content and sintering time on the relevant phase transformations were determined. Following sintering at 1373 K/30 MPa for 1–6 h, the NaZn13-type (La,Ce)(Fe,Co,Si)13 phase formed, the mass fraction of α-Fe phase reduced and the CeFe7-type (La,Ce)(Fe,Co,Si)7 phase appeared. The mass fraction of the (La,Ce)(Fe,Co,Si)7 phase increased, and the α-Fe phase content decreased with increasing Ce2Co7 content. However, the mass fraction of the (La,Ce)(Fe,Co,Si)7 phase reduced with increasing sintering time. The EDS results showed a difference in concentration between Co and Ce at the interphase boundary between the 1:13 phase and the 1:7 phase, indicating that the diffusion mode of Ce is reaction diffusion, while that of Co is the usual vacancy mechanism. Interestingly, almost 100 % single phase (La,Ce)(Fe,Co,Si)13 was obtained by appropriate Ce2Co7 addition. After 6 h sintering at 1373 K, the Ce and Co content in the (La,Ce)(Fe,Co,Si)13 phase increased for larger Ce2Co7 content. Therefore, the Curie temperature increased from 212 K (binder-free sample) to 331 K (15 wt.% Ce2Co7 sample). The maximum magnetic entropy change (−ΔSM)max decreased from 8.8 (binder-free sample) to 6.0 J/kg·K (15 wt.% Ce2Co7 sample) under 5 T field. High values of compressive strength (σbc)max of up to 450 MPa and high thermal conductivity (λ) of up to 7.5 W/m·K were obtained. A feasible route to produce high quality La(Fe,Si)13 based magnetocaloric composites with large MCE, good mechanical properties, attractive thermal conductivity and tunable TC by a one-step sintering process has been demonstrated.

1:13 phase formation mechanism and first-order magnetic transition strengthening characteristics in (La,Ce)Fe 13– x Si x alloys

Effect of Co Addition on the Phase Structure and Magnetic Properties of Fe-Si-Al Alloys

Phase Transition and Magnetocaloric Effect of LaFe11.5Si1.5Cx Compounds: Experiments and Density Functional Theory Calculations

One-Step Sintering Process for the Production of Magnetocaloric La(Fe,Si)13-Based Composites

Magnetocaloric effect and phase transformation of LaFe11.0M0.5Si1.5 (M = Cu, Ni, Mg) alloys

Enhanced Hard-Magnetic Properties and Thermal Stability of Nanocrystalline Ce-rich Ce-Fe-B Alloys by Combining La Substitution and Si Addition

Significant reduction of phase-transition hysteresis for magnetocaloric (La1-Ce )2Fe11Si2H alloys by microstructural manipulation

Suppressing the CeFe2 Phase Formation and Improving the Coercivity and Thermal Stability of Ce-Fe-B Alloys by Si Substitution

Rapid Formation of the Magnetocaloric Phase in La-Fe-Co-Si Magnetocaloric Alloys for Near Room Temperature Applications

Significant reduction of phase-transition hysteresis for magnetocaloric (La1-xCex)(2)Fe11Si2Hy alloys by microstructural manipulation

Clarifying the Basic Phase Structure and Magnetic Behavior of Directly Quenched (ce,la)2fe14b Alloys with Various Ce/La Ratios

Structure and Large Magnetic Entropy Change of Melt-Spun La1−xCex(Fe0.92Co0.08)11.4Si1.6 Alloys

Microstructure evolution and large magnetocaloric effect of La0.8Ce0.2(Fe0.95Co0.05)(11.8)Si-1.2 alloy prepared by strip-casting and annealing

Promoting the La Solution in 2:14:1-Type Compound: Resultant Chemical Deviation and Microstructural Nanoheterogeneity

Direct formation of La(Fe,Si)13 phase with enhanced mechanical property of off-stoichiometric La1.7Fe11.6Si1.4 alloys by directional solidification

Ce site dilution effects in the antiferromagnetic heavy fermion CeIn3

Microstructure, Phase Evolution and Magnetocaloric Properties of LaFe11.6Si1.4/La70Co30 Composite

Reduced Annealing Time and Enhanced Magnetocaloric Effect of La(Fe, Al) 13 Alloy by La-nonstoichiometry and Si-doping

Effect of partial substitution of Ce for La on the structural, magnetic and abnormal thermal expansion properties of La1-Ce Fe11.2Al1.8 alloys

Structure and Magnetocaloric Effect of La0.7ce0.3(Fe0.92co0.08)(11.4)Si-1.6 Bulk Alloy Prepared by Powder Metallurgy

Phase constitution, microstructure evolution and magnetocaloric properties of LaFe<sub>11.8</sub>Si<sub>1.2</sub> strip-casting flakes