Ferromagnetism with Strong Perpendicular Magnetic Anisotropy in Epitaxial SrMn0.3Ir0.7O3 Perovskite Films
Pengxiang Hou,Yiren Liu,Zhiyu Liu,Chuanhui Zhu,Yao Li,Zhongnan Xi,Yajie Han,Jiayi Li,Man-Rong Li,Jian Zhou,Lan Chen,Yu Deng,Yurong Yang,Jun-Ming Liu,Di Wu
DOI: https://doi.org/10.1103/physrevapplied.18.054083
IF: 4.6
2022-01-01
Physical Review Applied
Abstract:Strong Coulomb repulsion and spin-orbit coupling are known to give rise to exotic physical phenomena in transition metal oxides. Here, we report magnetic characteristics of a SrMn0.3Ir0.7O3 perovskite thin film, having both 3d and 5d elements on the B sites, with a strong perpendicular magnetic anisotropy (PMA), which is rare in perovskite oxide thin films. The SrMn0.3Ir0.7O3 films have been epitaxially deposited on (001)-oriented SrTiO3 single-crystal substrates by pulsed-laser deposition, exhibiting a para-to-ferromagnetic transition at about 110 K. The average valence of Mn and Ir cations are estimated as +3.61 and +4.17, respectively, by x-ray photoelectron spectroscopy. X-ray absorption spectroscopy reveals that Mn e(g) electrons occupy preferentially the d(3z2- r2) orbital, which produces the observed PMA in the framework of spin-orbital coupling. The SrMn0.3Ir0.7O3 thin film shows a large effective anisotropy constant of about 1.2x10(6) erg cm(-3) at 10 K, which is found to decrease with decreasing tetragonality c/a of the film. First-principles calculations reveal that Mn and Ir cations provide opposite magnetizations in SrMn0.3Ir0.7O3 and the Mn e(g) orbital polarization comes from both lattice distortion and oxygen octahedron rotation. The SrMn0.3Ir0.7O3 thin film with strong PMA may have applications in future low-power-consumption oxide spintronic devices.