First-Principles Prediction of Intermediate Products in the Decomposition of Metal Amidoboranes

Yongsheng Zhang,Tom Autrey,C. Wolverton

DOI: https://doi.org/10.1021/jp3106293

2011-01-01

Abstract:The nonvolatile products remaining after the thermal decomposition of metal amidoboranes (MAB, M = metal) are amorphous and incompletely characterized, increasing the complexity of devising regeneration strategies for these potential hydrogen storage materials. Utilizing the combined prototype electrostatic ground state search and density-functional theory (PEGS+DFT), we find that potential reaction products ([NHBH2](-), [NBH](-), [N3H2B3H3](-), and polymer-M[NHBH2] anion groups) in the decomposition of LiAB and CaAB are calculated to be significantly endothermic, in contrast to the experimentally measured nearly thermoneutral values [similar to-4 kJ/(mol H-2) in LiAB and 3.5 kJ/(mol H-2) in CaAB], suggesting that there are alternative products formed. The dianion group [NHBHNHBH3](2-) has recently been suggested to form in the decomposition of a calcium amidoborane complex in solution. In LiAB and CaAB, we use PEGS+DFT to predict intermediate metal-dianion compounds, and the static H-2 release enthalpy is 27.4 and 27.3 kJ/(mol H-2) in LiAB and CaAB, respectively. Introducing vibrational effects by phonon calculations, the enthalpies are shifted down by a roughly constant amount, similar to 25 and similar to 22 kJ/(mol H-2) at 0 and 300 K. Thus, our theoretical H-2 release enthalpies agree with the experimentally measured nearly thermoneutral data in the decomposition of LiAB and CaAB. This agreement supports the existence of the dianion phases as products in the decomposition of metal amidoboranes. Then, using the dianion compound as an intermediate in the decomposition of MAB, we further study the stability trends of a series of MAB (M = Li, Na, K, Ca).