Abstract:Ammonia is a carbon-free hydrogen carrier, and development of non-noble metal catalyst to decompose ammonia into hydrogen is desirable for practical applications. However, the metal catalyst is challenged by the sintering of metal particles under high-temperature reaction conditions. In this study, a series of Li-, Al-, and Co-containing hydrotalcite-like compounds (HTlc) were synthesized by co-precipitation and used as precursors to prepare well-dispersed and thermally stable Co nanoparticle catalysts for ammonia decomposition. The obtained precursors and catalysts were characterized by means of X-ray powder diffraction (XRD), temperature-programmed reduction (H 2 -TPR), X-ray photoelectron spectroscopy (XPS), high-angle annular dark-field scanning transmission electron microscopy (HAADF-STEM), and so on. All of the precursors formed hydrotalcite-like phase, which consisted of Li–Al–(Co) HTlc and/or Co–Al HTlc dependent on the Co content. Upon calcination at 500 °C, HTlc decomposed into an Al-substituted Co 3 O 4 spinel oxide, as confirmed by two distinctly separated reduction steps in H 2 -TPR. Following reduction at 700 °C, well-dispersed Co metal nanoparticles with an average particle size of ∼9.2–12.4 nm were obtained. It was suggested that the incorporation of Al 3+ into Co 3 O 4 led to a strong interaction between cobalt and aluminum, which suppressed the crystal growth of Co 3 O 4 and the sintering of Co metal during the thermal treatments, resulting in good Co dispersion. The optimal LiAlCo(1.5) catalyst showed superior activity than that prepared by impregnation method, giving almost complete conversion of ammonia at 575 °C under a space velocity of 5,000 mL g cat –1 h –1 . More importantly, this catalyst maintained stable activity at 625 °C for 100 h, exhibiting high stability and sintering resistance. The good catalytic performance was attributed to the high Co metal dispersion and strong metal–support interaction benefiting from the uniform distribution of cobalt in the HTlc precursor. These results demonstrate the applicability of HTlc to the preparation of metal catalysts with improved dispersion and thermal stability.

In Situ X-Ray Diffraction Study Of Co-Al Nanocomposites As Catalysts For Ammonia Decomposition

In‐situ Investigations of Co@Al2O3 Ammonia Decomposition Catalysts: The Interaction between Support and Catalyst

Synchrotron Radiation in Situ X-ray Absorption Fine Structure and in Situ X-ray Diffraction Analysis of a High-Performance Cobalt Catalyst Towards the Oxygen Reduction Reaction

Amorphous Co-B/Al Nanocomposites Prepared by Electroless Coating Technique and Their Excellent Catalytic Activity

Hydrotalcite-derived well-dispersed and thermally stable cobalt nanoparticle catalyst for ammonia decomposition

Dual Confinement of LaCoO x Modified Co Nanoparticles for Superior and Stable Ammonia Decomposition

Dual Confinement of LaCoOx Modified Co Nanoparticles for Superior and Stable Ammonia Decomposition

In Situ Production of Ni Catalysts at the Tips of Carbon Nanofibers and Application in Catalytic Ammonia Decomposition

Cobalt Nanoparticles Embedded in A Porous Carbon Matrix As an Efficient Catalyst for Ammonia Decomposition

An investigation of the thermal stability, crystal structure and catalytic properties of bulk and alumina-supported transition metal nitrides

Investigation of non-precious metal con4-based oxygen reduction catalyst by electrochemical and x-ray absorption spectroscopy techniques

Synergistic Catalysis of the Synthesis of Ammonia with Co-Based Catalysts and Plasma: From Nanoparticles to a Single Atom

Promoted Multimetal Oxide Catalysts for the Generation of Hydrogen Via Ammonia Decomposition

Ce0.6Zr0.3Y0.1O2 solid solutions-supported Ni Co bimetal nanocatalysts for NH3 decomposition

Combined in Situ Diffuse Reflectance Infrared Fourier Transform Spectroscopy and Kinetic Studies on CO2 Methanation Reaction over Ni/Al2O3

X-ray Absorption Spectroscopy Studies of a Molecular CO2-Reduction Catalyst Deposited on Graphitic Carbon Nitride

Non-Noble FeCrOx Bimetallic Nanoparticles for Efficient NH3 Decomposition

Chromium Oxide Catalysts for COx-free Hydrogen Generation Via Catalytic Ammonia Decomposition

Embedded MoN@C Nanocomposites As an Advanced Catalyst for Ammonia Decomposition to COx-free Hydrogen

Experimental and Theoretical Investigation of Molybdenum Carbide and Nitride As Catalysts for Ammonia Decomposition

Towards an Efficient CoMo/γ-Al 2 O 3 Catalyst Using Metal Amine Metallate As an Active Phase Precursor: Enhanced Hydrogen Production by Ammonia Decomposition