Advanced Configuration of N-Enriched Carbonized Tissue Paper as a Free-Standing Interlayer for Lithium–Sulfur Batteries at Wide-Range Temperatures
Rabia Khatoon,Yichuan Guo,Sanam Attique,Nasir Ali,Azim Uddin,Yang Tian,Haichao Tang,Xiang Gao,Qinggang He,Zhou Peng Li,Zhizhen Ye,Jianguo Lu
DOI: https://doi.org/10.1021/acsaem.1c02008
IF: 6.4
2021-09-08
ACS Applied Energy Materials
Abstract:Lithium–sulfur (Li–S) batteries with stable cyclic life, high sulfur loading greater than 70 wt % S, and operating in a wide range of temperatures have gained a competitive edge for promising applications. However, the low sulfur loading, shuttling effect, poor cycling stability, fast capacity fading, volume expansion, and limited operating temperature conditions limit their practical applications. Herein, we have designed a nitrogen-enriched functionalized carbon-based interlayer using waste tissue paper. The nitrogen-enriched interwoven fibrous interlayer sieved Li+ and confined the polysulfides within the high-sulfur (75 wt % S)-loaded cathodes. The battery exhibited a 1256 mA h g–1 capacity at 0.1C at 25 °C. At 1C, it attained 789 mA h g–1 and maintained 738 mA h g–1 over 500 cycles with a capacity retention of 72%. A wide range of temperatures from 0 to 70 °C is suitable for a Li–S battery. At 70 °C, the Li–S battery delivered an outstanding cyclic performance at 1C over 500 cycles with a capacity retention of 94.5%, an ultrahigh efficiency of 96%, and 0.01% capacity fade per cycle. Therefore, the facile strategy for the fabrication of the interlayer with the special network was effective for achieving high-performance Li–S batteries.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acsaem.1c02008.Thickness of free-standing CInLTp; XRD patterns and TGA curves of CInLTp, pristine sulfur, and the as-prepared cathodes of 75 wt % S, 80 wt % S, and 90 wt % S; electrochemical properties (CV, GCD, rate performance and cyclic tests) of 80 wt % S and 90 wt % S cathodes without and with CInLTp at 25 °C; EIS spectra for 80 and 90 wt % S batteries without and with CInLTp before and after 100 cycles; SEM images of 80 wt % S and 90 wt % S cycled cathodes without an interlayer; equivalent Nyquist circuit model for 75, 80, and 90 wt % S with and without CInLTp before and after 100 cycles; cycle test and equivalent Nyquist circuit model for 75 wt % S with CInLTp cathode at 70 °C at 1/10C; XPS spectra of pristine CInLTp and 75 wt % S without and with CInLTp before and after cycling; deconvoluted XPS spectra of N-1s; C-1s of 75 wt % S without and with CInLTp before and after cycling; EIS results of fitted equivalent Nyquist circuits for batteries without/with CInLTp electrodes operating at 25 °C; EIS results of fitted equivalent Nyquist circuits for batteries with CInLTp electrodes operating at 70 °C and 0 °C; and comparison of electrochemical performance of different interlayers (PDF)Strong stretching and expanding tendency of the cellulose-based fibers offer buffering to volume expansion (AVI)Volume expansion without the presence of the interlayer (AVI)This article has not yet been cited by other publications.
materials science, multidisciplinary,chemistry, physical,energy & fuels