Two softening stages in nanotwinned Cu

ligang sun,xiaoqiao he,linli zhu,jian lu

DOI: https://doi.org/10.1080/14786435.2014.977368

2014-01-01

Abstract:This study focuses on the deformation mechanisms of nanotwinned Cu with hierarchical twins (HTs) by virtue of a series of large-scale molecular dynamics (MD) simulations. For the same grain size d(G) and the same secondary twin spacing L-2, two softening stages and one strengthening stage are discovered, accompanied by the reduction of the primary twin spacing L-1. This special phenomenon is firstly found in nanotwinned Cu with HTs by MD simulations. In addition, totally different deformation mechanisms are observed along with the variation of L-1: (1) The transition of full dislocation to partial dislocation-dominated plastic deformation as the primary twin spacing L-1 decreases until L-1 reaches the first critical primary twin spacing [GRAPHICS] in the first softening stage. (2) The transition of partial dislocation to dislocation blockage-dominated plastic deformation leads to strengthening when the primary twin spacing L-1 is between the first critical primary twin spacing and second critical primary twin spacing [GRAPHICS] and [GRAPHICS] in the strengthening stage. (3) Partial dislocations parallel to the twin boundaries (TBs), detwinning and partial dislocation motion-induced thickening/thinning of TBs result in the second softening stage when the primary twin spacing L-1 is smaller than the second critical primary twin spacing [GRAPHICS] .