Fatigue and Cycle Plastic Behavior of 316laustenitic Stainless Steel under Asymmetric Load
Peng Jian,Gao Yi,Dai Qiao,Wang Ying,Li Kaishang
DOI: https://doi.org/10.11900/0412.1961.2018.00377
IF: 1.797
2019-01-01
ACTA METALLURGICA SINICA
Abstract:Due to excellent mechanical property and corrosion resistance of 316L austenitic stainless steel, it is widely used in chemical industry, but its fatigue behavior under asymmetric cycle load is not well understood. In this work, the fatigue and cyclic plastic deformation behavior of 316L austenitic stainless steel under asymmetric tensile-tensile cycle loading are studied, focusing on the variations of fatigue life, cycle plastic deformation and fracture mechanism with applied cycle load. The high and low stress regions can be clearly divided based on the differences of fatigue life, cyclic strain amplitude, mean strain, mean strain rate and failure strain. In the high stress region, mean strain, mean strain rate and failure strain are large, resulting in the significant cyclic plastic deformation, and the fatigue life is short. In the low stress region, the cyclic plastic deformation accumulation is limited, and the fatigue life is significantly increased. Through microstructural observations near fracture area and fracture surface analyses, the differences between large stress region and low stress region can be found. In the high stress region, a large number of voids are generated near the fracture surface, and the fracture surface is mainly featured by dimples. In contrast, in the low stress region, the fatigue crack is found near the fracture surface, and its propagation direction is perpendicular to the loading direction. The fatigue crack initiation site, the fatigue crack propagation zone, transition zone and rapid fracture zone are found on the fracture surface. Results of fracture mechanism analyses suggest that, the high stress region of 316L austenitic stainless steel is the cyclic plastic deformation dominant region, and the failure mechanism is the ductile failure caused by the accumulation of cyclic plastic deformation; while the low stress region is the fatigue dominant zone, and the failure mechanism is the fatigue crack propagation failure.