Abstract:In this work, the controlled epitaxial growth of ultrathin Pd shells of a few atomic layers (denoted as nL) on the surfaces of gold nanoparticle (Au NP) cores of different morphologies (trisoctahedral, cubic, and spherical shapes) in the presence of cetyltrimethylammonium chloride (CTAC) was achieved by regulating the pH value of the aqueous CTAC solution and finely tuning the amount of the Pd precursor. It was found that the critical shell thickness for epitaxial Pd growth at the optimal pH value was 4 atomic layers, taking {331}-faceted trisoctahedral (TOH) Au@Pd-nL NPs as an example, on the basis of the results of atomic-resolution high-angle annular dark-field scanning transmission electron microscopy (HAADF-STEM) images. Moreover, the resulting TOH Au@Pd-1L NPs (100.9 m(2) g(-1), 13.2 A mg(Pd)(-1) and 13.1 mA cm(-2)) exhibited excellent electrocatalytic performance and long-term electrocatalytic activity for ethanol oxidation, around 4.8-fold, 66-fold, and 21.8-fold better than commercial Pd/C catalysts (31 m(2) g(-1), 0.2 A mg(Pd)(-1), and 0.6 mA cm(-2)). Furthermore, the resulting TOH Au@Pd-1L NPs not only markedly enhance the chemical catalytic activity for the reduction of 4-nitrophenol (4-NP), but also allow the in situ surface-enhanced Raman spectroscopy (SERS) monitoring of the reaction process of the Pd-catalyzed reduction of 4-NTP. Thus, our work may provide a new way to fabricate core-shell (CS) bimetallic NPs with the merits of both metal outer shells (excellent catalytic performance in electrocatalysis and chemical catalysis) and Au NP cores (reaction process by in situ SERS monitoring).

Facile Fabrication of Porous Pd‐Au Bimetallic Nanostructures for Electrocatalysis

Enhancing the Catalytic and Electrocatalytic Properties of Pt-based Catalysts by Forming Bimetallic Nanocrystals with Pd

Trimetallic PtPdCo Mesoporous Nanopolyhedra with Hollow Cavities

Ph-Dependent Growth of Atomic Pd Layers on Trisoctahedral Gold Nanoparticles to Realize Enhanced Performance in Electrocatalysis and Chemical Catalysis

Electrocatalytic Activity of Bimetallic Platinum-Gold Catalysts Fabricated Based on Nanoporous Gold.

Facile Synthesis of Bimetallic Au@Pd Nanoparticles with Core-shell Structures on Graphene Nanosheets

Direct epitaxial growth of Au nanoparticles on Pd metallene enables robust oxygen reduction electrocatalysis

Engineering Porosity into Trimetallic PtPdNi Nanospheres for Enhanced Electrocatalytic Oxygen Reduction Activity

Atomically Dispersed Pt On Screw-Like Pd/Au Core-Shell Nanowires For Enhanced Electrocatalysis

Formation of Pd/Au Nanostructures from Pd Nanowires Via Galvanic Replacement Reaction

Enhancing the Electrocatalytic Activity of Pt-Pd Catalysts by Introducing Porous Architectures

Gold nanorod-templated synthesis of polymetallic hollow nanostructures with enhanced electrocatalytic performance.

Facile Fabrication Of Ultrathin Pt Overlayers Onto Nanoporous Metal Membranes Via Repeated Cu Upd And In Situ Redox Replacement Reaction

Synthesis of core/shell structured Pd3Au@Pt/C with enhanced electrocatalytic activity by regioselective atomic layer deposition combined with a wet chemical method

Controllable Synthesis Of Hierarchical Au/Pdag Heterostructures Consisting Of Nanosheets On Nanorods With Plasmon-Enhanced Electrocatalytic Properties

Synthesis of Branched Au‐PdAg Hybrid Nanosheets by Controlled Reduction in a Galvanic Replacement Reaction

Seeded growth of PdPtAg-on-Au heterogeneous nanoplates for efficient methanol oxidation Reaction: Interface engineering in quaternary metallic electrocatalysts

Synthesis of Ultrathin and Composition-Tunable PdPt Porous Nanowires with Enhanced Electrocatalytic Performance

Ultralong Pt-on-Pd bimetallic nanowires with nanoporous surface: nanodendritic structure for enhanced electrocatalytic activity.

Plasmonic synthesis of Non-homogeneous AuPd alloy for efficient electrocatalyst

Preparation of Au@Pd Core–Shell Nanorods with fcc -2H- fcc Heterophase for Highly Efficient Electrocatalytic Alcohol Oxidation