Abstract:To design new and efficient supramolecular recognition material, a macroporous organic–inorganic bis(n-amyloxy)calix[4]arene-crown-6 (BnACalix[4]C6) material for separation of cesium from acidic solution was developed. The results of SEM, TG–DSC, FT-IR, 29Si NMR, and XRD characterizations indicated that BnACalix[4]C6 molecules were successfully impregnated into the pores of SiO2–P support. Cs(I) was shown to be both strongly and selectively adsorbed by this material at 3.0 M HNO3. The total organic carbon values showed that the leakage of BnACalix[4]C6 from BnACalix[4]C6/SiO2–P was below 0.1 %. Thus, BnACalix[4]C6/SiO2–P is a promising candidate for separation of Cs(I) from acidic HAW in SPEC process.

Synthesis and Characterization of a Cesium-Selective Macroporous Silica-Based Supramolecular Recognition Material with High Stability