Covalent functionalization of activated MoS2 via using alkyl sulfide and their utilization in polymeric composites with mechanical and thermal property enhancements
Yunxia Li,Yiming Song,Dongchun Yang,Sheng Tian,Qin Deng,Xuegang Chen,Zhaobo Wang,Xin Wang,Haiqing Hu,Yilong Wang,Yong Tao,Jian Zhao
DOI: https://doi.org/10.1002/pc.27746
IF: 5.2
2023-10-05
Polymer Composites
Abstract:Schematic diagram of covalent functionalization of MoS2. Recently developed covalent functionalization of chemically exfoliated MoS2 (typically in alkyl lithium) allows the formation of chalcogenide‐carbon bonds by reacting with organohalides and aryl diazonium salts. We herein develop a novel method for the covalent functionalization of MoS2 to yield dodecylated MoS2 via reductive activation in a strongly reducing sodium‐naphthalene solution and using alkyl sulfide as an electrophile. Dodecylated MoS2/polystyrene (PS) composites fabricated by solution casting method. Dodecyl chains are grafted successfully onto MoS2 nanosheets, which gives rise to the exfoliation level of few‐layer thickness and matched compatibility with the host polymeric matrix. The inclusion of dodecylated MoS2 at a concentration of 1.0 wt% yields a substantial improvement in both Young's modulus and tensile strength, with a 106.7% increase and a 67% enhancement, respectively, as compared to the performance of pure PS. The enhanced mechanical characteristics can be credited to the uniform dispersion of dodecylated MoS2 within the PS matrix and enhanced interfacial interaction between the PS material and the filler. The composites demonstrate a significant increase in their glass transition temperature (Tg). Notably, the dodecylated MoS2/PS (1.0 wt%) composite exhibits a 59.8% elevation in storage modulus when compared to pure PS. The coke yield of dodecylated MoS2/PS (1.0 wt%) reaches 2.7%, much larger than the value (only 0.2%) for pure PS. The novel functionalization might expedite the applications of molybdenum disulfide in diverse fields. Highlights A novel method for the covalent functionalization of MoS2. Dodecylated MoS2/PS composites were fabricated via solution casting method. Ultrathin structure of MoS2 nanosheets was obtained after functionalization. Composites improvement in Young's modulus and tensile strength compared to PS. The composites show significant enhancements in Tg.
materials science, composites,polymer science