Enhancing the Performance of Rubber with Nano ZnO as Activators
Xuan Qin,Haoshu Xu,Ganggang Zhang,Jiadong Wang,Zhao Wang,Yuqi Zhao,Zongyu Wang,Tianwei Tan,Michael R. Bockstaller,Liqun Zhang,Krzysztof Matyjaszewski
DOI: https://doi.org/10.1021/acsami.0c15114
2020-10-11
Abstract:The vulcanization of rubber is a chemical process to improve the mechanical properties by cross-linking unsaturated polymer chains. Zinc oxide (ZnO) acts as an activator, boosting the rubbers' sulfur vulcanization. Maintaining the level of ZnO content in the rubber compounds as low as possible is desirable, not only for economic reasons but also to reduce the environmental footprint of the process. In this contribution, octylamine (OA) capped ZnO nanoparticles (5 nm diameter), prepared through a thermal decomposition method, were demonstrated to be efficient activators for the sulfur vulcanization of natural rubber, enabling the reduction of the required amount of ZnO as compared to commercial systems. The effect of different ZnO activators (OA capped ZnO/commercial indirect process ZnO) on the curing characteristics, cross-linking densities, and mechanical performance, as well as the thermal behavior of rubber compounds, were investigated. Compared to the commercial indirect process ZnO, OA capped ZnO nanoparticles not only effectively enhanced the curing efficiency of natural rubber but also improved the mechanical performance of the composites after vulcanization. This was interpreted as, by applying the OA capped ZnO nanoparticles, the ZnO levels in rubber compounding were significantly reduced under the industrial vulcanization condition (151 °C, 30 min).The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.0c15114?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.0c15114</a>.Materials and characterization methods; TGA curves for OA capped ZnO/rubber masterbatch composites; TGA and DLS curves, TEM images, and XRD pattern of OA capped ZnO nanoparticles; TEM images and XRD pattern of the commercial indirect process ZnO nanoparticles; the comparison of N<sub>2</sub> adsorption/desorption isothermal and pore size distribution of OA capped ZnO nanoparticles and the commercial indirect process ZnO nanoparticles; DSC curves of ZnO/natural rubber composites after vulcanization under different vulcanization conditions; vulcanization curves/stress–strain curves/cross-linking density of the ZnO/natural rubber composites; and tables of mechanical properties of ZnO/natural rubber composites and ZnO/styrene–butadiene rubber composites (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c15114/suppl_file/am0c15114_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology