Abstract:The surfactant-free emulsion polymerization (SFEP) of styrene and methyl methacrylate carried out in the aqueous solution of poly (ethylene glycol) (PEG) was studied. With high power optical microscope, Coulter counter and transmission electron microscopy,particle size, particle size distribution and zeta potential were measured in the process of polymerization. It is interesting to observe that the polymer particle size experiences a process from small to large, which can be more than 1000 mu m, and then from large to small, which is back to a range of 0. 04 0 similar to 0. 18 mu m. When the particle size returns to nanometer scale, the system has an obvious temperature rising. This phenomenon is different from the traditional nucleation mechanism of SFEP. The particle, which is formed by the homogeneous nucleation or oligomer micelle nucleation mechanism that is popularly received as traditional nucleation mechanism of SFEP, usually has a trend to become bigger and bigger to the end in the process of SFEP. It is obviously found that the freshly formed particles are first coalesced to form a particle pile, which is bigger than 1000 mu m and even seen with eyes, and then corrupted into tinny ones, which are smaller than 0. 04 mu m and even beyond the ability of high power optical microscope. With transmission electron microscopy (TEM), it was clearly proven the existence of paricle pile which was composed of a lot of little particles ranging from 40 nm to 80 nm. And by use of Coulter zeta potential measurement, it was found that the zeta potential of particles had a trend from low to high level, and experenced abruptly increase in zeta potential at 60 min which was just the time that the little particle seperated from the paricle pile. This phenomenan was very different from the system that SEEP was carryed out in water without PEG, in which the zeta potential of particle was keeping about -50 mV and just changed a little after 50 min. It was reasonble to think that the potential increase was the driving force to make the little particles to escape from the particle pile. Therefore, the mechanism of coalescence-separate nucleation is proposed.

Kinetics and mechanism of emulsifier‐free emulsion copolymerization

Kinetics and mechanism of emulsifier-free emulsion polymerization. III. Particle growth mechanism of seeded styrene/potassium persulfate system

Kinetics and mechanism of emulsifier-free emulsion polymerization: Styrene/surface active ionic comonomer system

Preparation of monodisperse polystyrene particles and assembly of spherical colloidal crystals

Kinetics and Mechanism of Emulsifier-Free Emulsion Polymerization. III. Styrene/nonionic Comonomer (2-Hydroxyethyl Methacrylate) System

Kinetics of N-Phenlymaleimide/Styrene/Acrylonitrile/ɑ-Methylstyrene Emulsion Copolymerization

Formation Mechanism of the Monodispersed Particles in the Emulsifier-Free Emulsion Polymerization ---- System of Methyl Methacrylate / Butyl Acrylate

STUDY ON THE FORMATION MECHANISM OF MONODISPERSE PARTICLES IN THE EMULSIFIER-FREE EMULSION POLYMERIZATION OF METHYL METHACRYLATE AND BUTYL ACRYLATE

Study on Kinetics of Styrene/Butyl Acrylate/Crosslinker Emulsion Copolymerization

Research of Styrene/Aerylonitrille/N-Phenlymaleimide Emalsion Copolymerization

Mechanism of Soap-Free Emulsion Polymerization of Styrene and 4-Vinylpyridine: Characteristics of Reaction in the Monomer Phase, Aqueous Phase, and Their Interface

Double roles of stabilization and destabilization of initiator potassium persulfate in surfactant-free emulsion polymerization of styrene under microwave irradiation.

Microemulsion polymerization of styrene initiated with potassium persulfate

Mini-emulsion formation and polymerization of styrene

Formation of Monodispersed Polymer Particles in Emulsifier-Free Emulsion Polymerization

Preparation of Polystyrene/Sio2 Composite Nanoparticles Bearing Sulfonic Groups on the Surface Via Emulsion Copolymerization Using A Polymerizable Emulsifier

Free radical seeded emulsion polymerization with participation of hydrolysis-condensation reaction ( Ⅱ ) Parameters and modeling application

Mechanism and Process of the Redispersion of the Aggregated Nano-Sio2 Particles During Emulsion Polymerization of Styrene

Preparation of Monodisperse Polystyrene Particles from Emulsifier-Free Miniemulsion Polymerization

A Comparative Study on Emulsion Polymerization Processes of Styrene Initiated by Water-soluble and Oil-soluble Initiators

PARTICAL SIZE EVOLUTION IN SURFACTANT-FREE EMULSION COPOLYMERIZATION OF STYRENE AND METHYL METHACRYLATE IN AQUEOUS SOLUTION OF POLY ( ETHYLENE GLYCOL)