Abstract:Flip-chip packaging on organic substrate has been used widely as a promising package technology for the next generation of electronic devices. However, due to its numerous interfaces (i. e. die/passivation, passivation/underfill, underfill/solder mask, and solder mask/circuit board), it is more susceptible to a variety of complexworking and testing environments, delamination can easily take place in some critical sites, which is one of the greatest threats to its reliability. In this paper, delamination initiation and propagation behaviors of horizontal and vertical chip/underfill interfaces under temperature cycling tests are analyzed respectively by using cohesive zone model (CZM). The results indicate that delamination will occur first along the horizontal interface between chip and underfill and even when it propagates about 0.13mm, delamination still have not taken place at vertical interface. What's more, variance of phase angle with testing time and crack length is investigated. It turns out that when the crack is short, shearing stress dominates the contribution to causing the interfacial delamination, however, when the crack becomes long, the peeling stress gradually turns to be in the same range or even higher than that of shearing stress. Compared with interfacial delamination in vertical direction, the horizontal one induces a bigger threat to the reliability of flip-chip package because once it propagates to the solder joints, the fatigue life of solder would be reduced rapidly. The effect of interfacial delamination on fatigue life of solders is also implemented in this paper. It is found that plastic strain has been more than doubled in one temperature cycle when interfacial delamination is induced. Fatigue life is estimated by using modified Coffin-Mansin equation. It is found that induced interfacial delamination can decrease the solder's life by about 93.5%. Furthermore, the imperfection of underfill layers and some voids in the corners of the solder joints caused by the contamination of the flux residues in the corners of the solder joints are also taken into account. And the incremental inelastic strain caused by the voids is compared with that induced by interfacial delamination. It is found that interfacial delamination can lead to much higher plastic strain, that is to say, compared with process-induced defects, delamination has a much greater impact on solder's fatigue life and the whole package's reliability.

Adhesion Reliability of the Epoxy-Cu Interface by Molecular Simulations

Estimating Interfacial Interaction Energy of Cu-epoxy Resin from Molecular Dynamics Simulation

Adhesion improvement of Cu-based substrate and epoxy molding compound interface by hierarchical structure preparation

Study on Interfacial Interaction Energy of Cu–SAM–epoxy Systems in a Hot and Humid Environment

Electronic Interaction of Epoxy Resin with Copper at the Adhered Interface

Moisture effect on interfacial integrity of epoxy-bonded system: a hierarchical approach.

Study The Mixed-Mode Delamination Of The Epoxy/Cu Interface

Molecular Dynamics Study on the Tensile Deformation of Cross-Linking Epoxy Resin

The Effect of Pressure and Orientation on Cu-Cu3Sn Interface Reliability under Isothermal Ageing and Monotonic Traction Via Molecular Dynamics Investigation

The Effect Of Cu Orientation On Fracture Location In Cu3sn-Cu Interface Structure Under Monotonic Loading Condition By Molecular Dynamics Simulation

Interfacial Delamination Characterization and Thermo-mechanical Reliability of Stacked Die Package by Finite Element Analysis

Effects of high temperature and high humidity on the reliability of copper/epoxy bond

Unraveling disadhesion mechanism of epoxy/CSH interface under aggressive conditions

A Molecular Dynamics Investigation on the Compression of Cross-Linked Epoxy Resins

Interfacial Delamination Analysis At Chip/Underfill Interface And Investigation Of Its Effect On Flip-Chip'S Reliability

A Study on Hygrothermal Degradation and Recovery of an Epoxy Adhesive Using Molecular Dynamics Simulation

Molecular Understanding of the Distinction between Adhesive Failure and Cohesive Failure in Adhesive Bonds with Epoxy Resin Adhesives

Probing Interfacial Aging of Model Adhesion Joints under a Hygrothermal Environment at a Molecular Level.

Theoretical investigation of epoxy detachment from C-S-H interface under aggressive environment

Study on the Mixed-Mode Fracture of the Epoxy-Cu Interface

Investigation of Moisture Influence on Structure and Thermal Conductivity of Epoxy Resin by Molecular Dynamics Simulation