Abstract:(NaxLaxPb1−2x)(Lu1/2Nb1/2)O3 antiferroelectric (AFE) ceramics (x=0, 0.01, 0.02, 0.03, 0.04, 0.05) were successfully obtained by solid state reactions. The structural phase transitions and the electrical behavior have been investigated. XRD analysis indicates that La3+ and Na+ have diffused into the lattices and the ceramics display a pure perovskite structure. It is found Curie temperature TC for AFE transition decreases from 270°C to 242°C with increasing of Na+ and La3+ content, similarly, the dielectric constant (ε′) decreases from 677 to 390. Compared to LaxPb1−3x/2(Lu1/2Nb1/2)O3 AFE ceramics, the energy storage performance was enhanced about 7%, and the maximum value of energy storage density was calculated up to 4.12J/cm3 at 200°C.

Structure and Properties of (na La Pb1−2)(Lu1/2Nb1/2)O3 Antiferroelectric Ceramics