Preparation of quantum dot luminescent materials through the ink approach

Wenjun Wei,Heng Xu,Qingliang You,Qi Cheng,Cui Liu,Linling Zou,Xueqing Liu,Jiyan Liu,Yuan-Cheng Cao,Guang Zheng

DOI: https://doi.org/10.1016/j.matdes.2015.11.077

IF: 9.417

2016-01-01

Materials & Design

Abstract:Highly transparent and luminescent UV curable polyurethane acrylate/quantum dot (QD) nanocomposite material was prepared using “QD inks” approach by UV curing. First, water soluble CdTe QDs (λem=510nm, 540nm and 620nm) were synthesized. Urethane acrylate prepolymer was used as the media for the “QD ink” and 2-hydroxy-2-methylpropiophenone (HMPF, also called 1173) was used as the photoinitiator. FT-IR spectra showed that there were strong vibrations at 1725cm−1 which was contributed from the –CO groups after the polymerization, while the end –CCH2 group vibration at 964cm−1 and 993cm−1 disappeared. Thermogravimetric analysis of the resultants showed the 5% weight loss up to 150°C which was the free water content; and 9.18% loss of the weight was the dehydrate of the resins in 150°C–301.75°C; weight loss of 93% from 300°C to 450°C was the decomposition. Mechanical tests showed that the elongation at break was 12.96%, and that the tensile strength was 5.39MPa. This “QD ink” approach is attractive in the preparation of luminescent materials and thus is prospective in the development of QD devices.