Comparative study on superplastic tensile behaviors of the as-extruded Ti6Al4V alloys and TiBw/Ti6Al4V composites with tailored architecture

l j huang,c j lu,b yuan,s l wei,x p cui,l geng

DOI: https://doi.org/10.1016/j.matdes.2015.12.162

IF: 9.417

2016-01-01

Materials & Design

Abstract:The superplastic tensile behaviors and mechanisms of Ti6Al4V alloys and TiBw/Ti6Al4V composites with tailored architecture were comparatively studied in order to reveal the superplasticity mechanisms. The superplastic tensile tests were carried out at the temperatures of 900°C, 925°C, 950°C and 975°C with the strain rate of 0.000316/s, 0.001/s and 0.00316/s, respectively. The composites exhibited higher superplasticity, higher strain rate sensitivity index m and lower activation energy Q than the alloys. This might be attributed to the small lamellar aspect ratio and TiBw reinforcement addition. Microstructural observation showed that the aspect ratio of α phase in the Ti6Al4V alloys decreased with increasing strains, and transferred to equiaxed grains only in the tip area. Therefore, necking could not be constrained and transferred to other positions with unfavorable microstructure, led to the needle-like fracture macro morphology. On the contrary, the TiBw/Ti6Al4V composites had weak necking tendency due to the globalization process completed at small strain, which contributed to the large elongations. Recrystallization should be responsible for the decrease in lamellar aspect ratio and increase in volume fraction of β phase, which are considered to be the major coordination mechanism of superplasticity for the as-extruded TiBw/Ti6Al4V composites.