Hot deformation characteristics and processing parameter optimization of 2219 Al alloy using constitutive equation and processing map
Hailin He,Youping Yi,Jindong Cui,Shiquan Huang
DOI: https://doi.org/10.1016/j.vacuum.2018.11.048
IF: 4
2019-02-01
Vacuum
Abstract:Isothermal compression tests of the as-homogenized 2219 Al alloy were conducted at temperatures of 260–510 °C and strain rates of 0.001–10 s−1 to study the hot deformation characteristics and obtain the optimum processing window for the alloy. This material is of significant interest in the aerospace industry, and in-depth understanding its behavior during processing is essential to avoid structural defects and ensure high-quality components. In the strain–stress curves, the stress increased to a plateau without a clear peak stress, which is typical of dynamic recovery, and a constitutive equation was established to describe the steady flow stress of the alloy. The developed processing map indicated that instability domains were more likely to occur in regions with a higher Zener–hollomon (Z) parameter, and the hot-working domain corresponding to 380–510 °C and 0.008–0.78 s−1, which was in the stability region with high efficiency and/or high dynamic recovery rate, was recommend for hot processing of the alloy. The softening mechanism of this alloy is mainly dynamic recovery, as evidenced by microstructural observations showing many subgrains with low-angle grain boundaries. In addition, some new, fine grains with high-angle grain boundaries also formed during hot deformation. The primary mechanism of formation of these new grains was continuous dynamic recrystallization (CDRX), and the most efficient CDRX was obtained at moderate Z values.
materials science, multidisciplinary,physics, applied