Abstract:Facile synthesis of Au–Pt bimetallic nanoparticles (Au1−xPtx NPs) and mixtures of Au NPs and Pt NPs ((100 % − y)Au/yPt NPs) and their subsequent deposition on nest-like MnO2 nanostructures were presented. The as-prepared products were characterized by means of UV–visible spectroscopy, X-ray diffraction, scanning and transmission electron microscopy, and energy dispersive spectroscopy. TEM analyses showed that noble metal NPs were evenly dispersed on the surface of nest-like MnO2 nanostructures and no agglomeration was observed. The as-prepared metal NPs supported catalysts showed higher catalytic activities than MnO2 nanostructures for oxidative decomposition of formaldehyde (HCHO). The forms of noble metal NPs and Au/Pt molar ratio have significant effects on the catalytic performance, and Au0.5Pt0.5/MnO2 has the highest catalytic activity among all the as-prepared metal NPs supported MnO2 catalysts, and the temperature for complete decomposition of HCHO reached as low as 313 K. The high catalytic activities of Au1−xPtx/MnO2 catalysts resulted from the synergistic effect between Au1−xPtx NPs and MnO2 nanostructure, as well as the synergistic effect between Au and Pt. The current Au1−xPtx/MnO2 catalysts are among the first trials to apply bimetallic NP-supported catalysts to the decomposition of HCHO, and proved that the Au1−xPtx/MnO2 catalysts are promising for indoor decomposition of formaldehyde due to their easy synthesis, low cost, and excellent catalytic performance.

Highly Dispersed and Active Supported Pt Nanoparticles for Gaseous Formaldehyde Oxidation: Influence of Particle Size

Complete Elimination of Indoor Formaldehyde over Supported Pt Catalysts with Extremely Low Pt Content at Ambient Temperature

Effect of Reduction Treatment on Structural Properties of Tio2 Supported Pt Nanoparticles and Their Catalytic Activity for Formaldehyde Oxidation

Enhanced Formaldehyde Oxidation Performance of the Mesoporous TiO(B)-Supported Pt Catalyst: The Role of Hydroxyls.

Removal of Formaldehyde Using Highly Active Pt/TiO2 Catalysts Without Irradiation

Mechanistic Study on Formaldehyde Removal over Pd/TiO2 Catalysts: Oxygen Transfer and Role of Water Vapor

Complete Oxidation of Formaldehyde at Room Temperature Using Tio2 Supported Metallic Pd Nanoparticles

Enhanced Catalytic Activity Of Hierarchically Macro-/Mesoporous Pt/Tio2 Toward Room-Temperature Decomposition Of Formaldehyde

Effect of Support (degussa P25 TiO2, Anatase TiO2, Γ-Al2o3, and AlOOH) of Pt-based Catalysts on the Formaldehyde Oxidation at Room Temperature

Efficient Decomposition of Formaldehyde on Ni−Al Hydrotalcite/AlOOH Nanocomposites Decorated with Pt Nanoparticles at Ambient Temperature

A Facile Route for Spraying Preparation of Pt/TiO2 Monolithic Catalysts Toward VOCs Combustion

Hierarchical Ni−Al Hydrotalcite Supported Pt Catalyst for Efficient Catalytic Oxidation of Formaldehyde at Room Temperature

Effect of oxygen mobility in the lattice of Au/TiO 2 on formaldehyde oxidation

Graphene Oxide/fe2o3 Nanoplates Supported Pt for Enhanced Room-Temperature Oxidation of Formaldehyde

Engineering stable Pt nanoclusters on defective two-dimensional TiO2 nanosheets by introducing SMSI for efficient ambient formaldehyde oxidation

Efficient elimination of formaldehyde over Pt/Fe3O4 catalyst at room temperature

Deactivation and Regeneration of Pt/Tio2 Nanosheet-Type Catalysts with Exposed (001) Facets for Room Temperature Oxidation of Formaldehyde

Selective oxidation of glycerol in a base-free aqueous solution over different sized Pt catalysts

The Size Effect and High Activity of Nanosized Platinum Supported Catalysts for Low Temperature Oxidation of Volatile Organic Compounds

Facet- and defect-engineered Pt/Fe2O3 nanocomposite catalyst for catalytic oxidation of airborne formaldehyde under ambient conditions

Au–Pt bimetallic nanoparticles supported on nest-like MnO2: synthesis and application in HCHO decomposition