Adsorption/desorption performance of cellulose membrane for Pb(ii)
Bai-Yun Zhao,Jiao-Jiao He,Li Wang
DOI: https://doi.org/10.1515/gps-2023-0014
2023-01-01
Green Processing and Synthesis
Abstract:Abstract Cellulose membrane (CM) was successfully prepared by phase conversion (L–S). The adsorption performance of CM for Pb( ii ) under different adsorption conditions was investigated, and the adsorption isothermal models and kinetic models were established. Additionally, desorption performance of CM for Pb( ii ) under different conditions were also investigated. Scanning electron microscope (SEM), energy dispersion spectroscopy (EDS), and Fourier transform infrared (FT-IR) methods were used to evaluate changes in the microstructure, element content, and functional groups of CM. The maximum adsorption capacity (343 mg·g −1 ) of Pb( ii ) was achieved (initial concentration of Pb( ii ) solution was 1,200 mg·L −1 , pH was 4.5, adsorption time was 120 min, adsorption temperature was 30°C). Meanwhile, the process conforms to multi-molecular layer chemical adsorption. The desorption results showed that the maximum desorption capacity was 90.00 mg·g −1 (HNO 3 concentration was 0.04 mol·L −1 , desorption time was 120 min, desorption temperature was 60°C). SEM showed that the pores were saturated after adsorption of Pb( ii ). Mapping and EDS analysis revealed that CM contained 72.14% Pb( ii ) after adsorption. In the FT-IR curve, Pb( ii ) chelated the C═O group of the CM. This method showed great potential for adsorption of Pb( ii ) from aqueous solutions.
engineering, chemical,green & sustainable science & technology,chemistry, multidisciplinary