Abstract:In this study, a core–shell catalyst of Cu-SAPO-34@Fe-MOR was successfully prepared through a silica-sol adhesion method, and its performance for selective catalytic reduction of nitric oxide by NH 3 (NH 3 -SCR) was evaluated in detail. The Fe-MOR coating has not only increased the high-temperature activity and broadened the reaction temperature window of Cu-SAPO-34 to a large extent, but also increased the hydrothermal stability of Cu-SAPO-34 markedly. It is demonstrated that a strong synergistic interaction effect exists between Cu 2+ and Fe 3+ ions and promotes the redox cycle and oxidation–reduction ability of copper ions, which greatly accelerates the catalytic performance of the core–shell Cu-SAPO-34@Fe-MOR catalyst. Abundant isolated Cu 2+ ions and Fe 3+ ions on the ion exchange sites performing NO x reduction at low and high temperature region lead to the broad reaction temperature window of Cu-SAPO-34@Fe-MOR. In addition, more weakly adsorbed NO x species formed and the increased number of Lewis acid sites may also contribute to the higher catalytic performance of Cu-SAPO-34@Fe-MOR. On the other hand, the better hydrothermal ageing stability of Cu-SAPO-34@Fe-MOR is related to its lighter structural collapse, fewer acidic sites lost, more active components (Cu 2+ and Fe 3+ ) maintained, and more monodentate nitrate species formed in the core–shell catalyst after hydrothermal ageing. Last, the mechanism study has found that both Langmuir–Hinshelwood ("L–H") and Eley–Rideal ("E–R") mechanisms play an essential role in the catalytic process of Cu-SAPO-34@Fe-MOR, and constitute another reason for its higher activity compared with that of Cu-SAPO-34 (only "L–H" mechanism).

The influence of CO 2 and H 2 O on selective catalytic reduction of NO by NH 3 over Cu/SAPO-34 catalyst

Unexpected Promotion Effect of H 2 O on the Selective Catalytic Reduction of NO x with NH 3 over Cu-SSZ-39 Catalysts

Insight into the catalytic performance and NH3 adsorption under high concentration of CO2 and/or H2O conditions on selective catalytic reduction of NO by NH3 over V2O5-WO3/TiO2 catalyst

Effect of No2 on the Selective Catalytic Reduction of No with Nh3 over Cu/Sapo-34 Molecular Sieve Catalyst

Location and Nature of Cu Species in Cu/SAPO-34 for Selective Catalytic Reduction of NO with NH3

Understanding the Water Effect for Selective Catalytic Reduction of NOx with NH3 over Cu-SSZ-13 Catalysts

Effect of H2o on No Reduction over Nsr Catalyst 12cao Center Dot 7Al(2)o(3)/10%k

Effects of Water Vapor, Co2 and So2 on the No Reduction by Nh3 over Sulfated Cao

Promoting effects of water on the NH3-SCR reaction over Cu-SAPO-34 catalysts: transient and permanent influences on Cu species

Mechanism of NO reduction by NH3 over MnCuOx catalysts and the influence mechanism of CO

Effects of H2O and SO2 on the Performance of V2O5/TiO2 Catalysts for Selective Catalytic Reduction of NO in Flue Gas

Structure-activity relationship and the inhibitory effect of sulfur dioxide and water on nitrous oxide formation in selective catalytic reduction of nitrogen oxides by ammonia over hollow Co<sub>3</sub>O<sub>4</sub>@CoMn<sub>2</sub>O<sub>4</sub> catalyst

Comparison Study of Cu-Fe-Ti and Co-Fe-Ti Oxide Catalysts for Selective Catalytic Reduction of NO with NH3 at Low Temperature

Effective reduction of nitric oxide over a core–shell Cu-SAPO-34@Fe-MOR zeolite catalyst

Effect of Water on the Performance of Silica-Pillared Layered Niobate-Supported Copper Oxide Catalyst for NO Reduction by CO

Effect of reduction on NO + CO reaction performance of CuO-Co3O4 symbiotic oxide porous nanosheet and DFT calculation

Recent Advances of Cu-Based Catalysts for NO Reduction by CO under O2-Containing Conditions

The Effects of H2o and So2 on the Behaviour of Cuso4-Ceo2/Ts for Low Temperature Catalytic Reduction of No with Nh3

Effects of water vapor, CO 2 and SO 2 on the NO reduction by NH 3 over sulfated CaO

Effect of Cu loading on the performance and kinetics of Cu/SAPO-34 catalysts for selective catalytic reduction with NH3

Experimental and Modeling Analysis of NO Reduction by CO for a FCC Regeneration Process