Unique three-dimensional hierarchical heterogeneous MoS2/graphene structures as a high-performance anode material for lithium-ion batteries
Fei Long,Yi Chen,Caihong Wu,Jilin Wang,Shuyi Mo,Zhengguang Zou,Guoyuan Zheng
DOI: https://doi.org/10.1007/s11581-021-03936-y
IF: 2.961
2021-03-12
Ionics
Abstract:<p class="a-plus-plus">A unique MoS<sub class="a-plus-plus">2</sub>/graphene composite (MoS<sub class="a-plus-plus">2</sub>/GrF) was synthesized via a facile hydrothermal method. XRD, FESEM, EDS, TEM, HRTEM, XPS, and BET analyses were performed to characterize the as-synthesized samples. The samples were demonstrated to present interesting uniform three-dimensional hierarchical heterogeneous structures where MoS<sub class="a-plus-plus">2</sub> microspheres (with an average diameter of 750 nm) penetrated the graphene layer. By the "space-confined" effect, the (002) plane of MoS<sub class="a-plus-plus">2</sub> is inhibited when grown in the interlayer of GO, which increases the interlayer spacing and improves the rate performance of the electrode. Moreover, MoS<sub class="a-plus-plus">2</sub> that grows between the graphene layers can form a good contact, reducing the contact resistance. As an anode material for lithium-ion batteries, the MoS<sub class="a-plus-plus">2</sub>/GrF electrode exhibited an outstanding reversible capacity (1510 mAh g<sup class="a-plus-plus">−1</sup> at 100 mA g<sup class="a-plus-plus">−1</sup> after 200 cycles) and excellent rate performance (~990 mAh g<sup class="a-plus-plus">−1</sup> at 1000 mA g<sup class="a-plus-plus">−1</sup>).</p>
chemistry, physical,physics, condensed matter,electrochemistry