Abstract:Herein, we reported a well-controlled hydrothermal synthesis of Co3O4 nanowires using CoSO4 as a cobalt precursor and glycerol as a morphological directing agent. Scanning electron microscopy was employed to observe the growth of nanowires. As an important synthetic parameter, reaction time is spanned from 4 to 24 h, which played an important role in the morphology and properties of materials. When the reaction time was 4 h, the resulting Co3O4 nanoparticles assembled into some short nanorods. While increasing the reaction time, the nanorods grew into long nanowires with large aspect ratio, and then attached into bundles when the reaction time was extended up to 24 h. Electrochemical characterization shows that Co3O4 nanowires prepared by hydrothermal reaction for 12 h exhibited the highest catalytic activity for oxygen evolution reaction (OER) among all synthesized nanowires and nanoparticles using the similar method. The enhanced OER activity of the 12 h-prepared Co3O4 nanowires should be attributed to the increased electroactive surface area because observed from the cyclic voltammogram, the 12 h-prepared Co3O4 nanowires possessed the highest surface area among all tested samples. It was also illustrated that there existed a close correlation of the OER catalytic activity with the transition of oxidation state and the density of activity sites of the catalyst exposing to the electrolyte solution during the electrolysis. Though both Co3O4 nanowires and nanoparticles exhibited a considerable loss in OER activity during the stability testing, after polarization for 4 h at 1.7V (versus a reversible hydrogen electrode), the Co3O4 nanowires still produced the higher catalytic current than that of the Co3O4 nanoparticles showing a slightly higher stability than the particles because of the nanowire structure. Published by AIP Publishing.

Mesoporous Nanobelts And Nano-Necklaces Of Co3o4 Converted From Beta-Co(Oh)(2) Nanobelts Via A Thermal Decomposition Route For The Electrocatalytic Oxidation Of H2o2

Electrocatalysis: Reduced Mesoporous Co3O4 Nanowires as Efficient Water Oxidation Electrocatalysts and Supercapacitor Electrodes (Adv. Energy Mater. 16/2014)

Topotactic Conversion Route to Mesoporous Quasi-Single-Crystalline Co<sub>3</sub>O<sub>4</sub>Nanobelts with Optimizable Electrochemical Performance

Composite Nanoarchitectonics of Co3O4 Nanopolyhedrons with N-Doped Carbon and Carbon Nanotubes for Alkaline Oxygen Evolution Reaction

From Cobalt Nitrate Carbonate Hydroxide Hydrate Nanowires To Porous Co3o4 Nanorods For High Performance Lithium-Ion Battery Electrodes

Topotactic Conversion Route to Mesoporous Quasi‐Single‐Crystalline Co3O4 Nanobelts with Optimizable Electrochemical Performance

Co(Oh)(3) Nanobelts: Synthesis, Characterization and Shape-Preserved Transformation to Pseudo-Single-Crystalline Co3o4 Nanobelts

Hydrothermal Synthesis of Mesoporous Co3O4 Nanobelts by Means of a Compound Precursor

Morphology-controlled Synthesis of CoMoO4 Nanoarchitectures Anchored on Carbon Cloth for High-Efficiency Oxygen Oxidation Reaction

Mesoporous Co3 O4 Nanobundle Electrocatalysts.

Mesoporous Co3O4 and CoO@C Topotactically Transformed from Chrysanthemum-like Co(CO3)0.5(OH)center dot 0.11H2O and Their Lithium-Storage Properties

Co/CoOx Nanoparticles Embedded on Carbon for Efficient Catalysis of Oxygen Evolution and Oxygen Reduction Reactions.

Novel synthesis of <i>in situ</i> CeO<sub><i>x</i></sub> nanoparticles decorated on CoP nanosheets for highly efficient electrocatalytic oxygen evolution

Simple hydrothermal synthesis of mesoporous spinel NiCo<sub>2</sub>O<sub>4</sub>nanoparticles and their catalytic behavior in CH<sub>3</sub>OH electro-oxidation and H<sub>2</sub>O<sub>2</sub>electro-reduction

Morphology-controlled Fabrication of Co3O4 Nanostructures and Their Comparative Catalytic Activity for Oxygen Evolution Reaction

Mesoporous Nanosheet Networked Hybrids of Cobalt Oxide and Cobalt Phosphate for Efficient Electrochemical and Photoelectrochemical Oxygen Evolution.

Co2(OH)3Cl and MOF mediated synthesis of porous Co3O4/NC nanosheets for efficient OER catalysis

Uniformly Grown PtCo-modified Co3O4 Nanosheets As a Highly Efficient Catalyst for Sodium Borohydride Electrooxidation

Novel cobalt nanorods@ cobalt-platinum nanoparticles for electrocatalytic hydrogen evolution reactions and oxygen evolution reactions study

Synthesis of Mesoporous Co3O4 Nanosheet-Assembled Hollow Spheres Towards Efficient Electrocatalytic Oxygen Evolution

Hydrothermal Synthesis of Co3o4 Nanowire Electrocatalysts for Oxygen Evolution Reaction