Enhanced Multiferroic and Dielectric Properties of Sr2+-doped BiFe0.94(Mn0.04Cr0.02)O3 Thin Films

Guoqiang Tan,Wenlong Liu,Guohua Dong,Xu Xue,Huijun Ren,Ao Xia

DOI: https://doi.org/10.1007/s10854-014-2174-x

2014-01-01

Journal of Materials Science Materials in Electronics

Abstract:Sr2+-doped B1−xSrxFe0.94(Mn0.04Cr0.02)O3 (B1−xSrxFMC, x = 0.00, 0.05 and 0.09) thin films were prepared on FTO/glass (SnO2: F) substrates by using a sol–gel spin-coating method. X-ray diffraction (XRD), Rietveld refined XRD data and Raman scattering spectra illustrate a structural evolution from trigonal (R3c: H) to tetragonal (P4) occurs in B1−xSrxFMC thin films with the increase of Sr2+ concent. Superiorly multiferroic and dielectric properties were obtained in the B1−xSrxFMC thin films, e.g., large remanent polarization value, a high dielectric constant (P r = 139.21 μC/cm2 and εr = 396.7 for x = 0.09) and large saturation magnetization (M s = 2.08 emu/cm3 for x = 0.05). The leakage current density of B1−xSrxFMC thin films is increased with increasing Sr2+ concentration, wherein the leakage current density of all the B1−xSrxFMC films is of the order of magnitude of 10−5 A/cm2, which are still lower than that in the pure BFO film (10−3 A/cm2).