Mechanism of local stress field on the enhancement of pyroelectric performance of PNZST:AlN Composite Ceramics
Ling Li,Tianze Pan,Jiajun Ma,Shan-Tao Zhang,Yaojin Wang
DOI: https://doi.org/10.7498/aps.71.20221250
IF: 0.906
2022-01-01
Acta Physica Sinica
Abstract:In this paper, composite ceramics (1-<i>x</i>)Pb<sub>0.99</sub>Nb<sub>0.02</sub>[(Zr<sub>0.57</sub>Sn<sub>0.43</sub>)<sub>0.94</sub>Ti<sub>0.06</sub>]<sub>0.98</sub>O<sub>3</sub>:<i>x</i>AlN (abbreviated (1-<i>x</i>)PNZST:<i>x</i>AlN, <i>x</i>=0, 0.1, 0.2, 0.3 and 0.4) were prepared by a two-step solid phase synthesis method. The crystal structure, micromorphology, domain structure evolution, as well as the ferroelectric, dielectric and pyroelectric properties of composite ceramics were systematically investigated. The results show that the difference of thermal expansion coefficients of PNZST and AlN leads to compressive stresses in the PNZST matrix when cooling down from the sintering temperature, then a metastable ferroelectric (FE) phase was induced in the anti-FE matrix by the AlN component-induced internal stress, and in turn ferroelectric/antiferroelectric phase boundary was constructed near room temperature, as the temperature increases, the ferroelectric→antiferroelectric phase transition causes a larger pyroelectric current peak. In particular, the composition with <i>x</i>=0.1 exhibit high pyroelectric coefficient with <i>p</i>=33.0<teshuzifu>x10<sup>-4</sup> C<teshuzifu>×m<sup>-2</sup><teshuzifu>×K<sup>-1</sup> and figures of merit with current responsivity <i>F</i><sub>i</sub>=31.6<teshuzifu>x10<sup>-10</sup> m<teshuzifu>×V<sup>-1</sup>,voltage responsivity <i>F</i><sub>v</sub>=61.3<teshuzifu>x10<sup>-2</sup> m<sup>2</sup><teshuzifu>×C<sup>-1</sup>, and detectivity <i>F</i><sub>d</sub>=44.0<teshuzifu>x10<sup>-5</sup>Pa<sup>-1/2</sup> around human body temperature. Moreover, the enhanced pyroelectric coefficients exist in a broad operation temperature range with a large full width at half maximums of 16.3℃ at 37℃. As the increase of AlN content, the pyroelectric peak temperature of the composite ceramic is adjustable in a wide temperature range of 37-73℃, showing good temperature stability.