Abstract:Transition-metal-doped ${\mathrm{Bi}}_{2}$${\mathrm{Sr}}_{1.8}$${\mathrm{La}}_{0.2}$${\mathrm{Cu}}_{1\mathrm{\ensuremath{-}}\mathit{x}}$${\mathit{M}}_{\mathit{x}}$${\mathrm{O}}_{\mathit{y}}$ (M=Fe, Co, Ni, and Zn) samples were synthesized. X-ray diffraction analysis showed that these 3d elements had different solubility in ${\mathrm{Bi}}_{2}$${\mathrm{Sr}}_{1.8}$${\mathrm{La}}_{0.2}$${\mathrm{CuO}}_{\mathit{y}}$. The limits of solid solution formation were at x=0.5 for the Fe system, x=1.0 for the Co system, and x=0.1 for the Ni and Zn systems. The effect of these 3d metal substitutions for Cu on the incommensurate modulation structure in ${\mathrm{Bi}}_{2}$${\mathrm{Sr}}_{1.8}$${\mathrm{La}}_{0.2}$${\mathrm{CuO}}_{\mathit{y}}$ was examined by means of electron diffraction. The experimental results showed that all the substitutions of Fe, Co, Ni, and Zn for Cu decreased the modulation periodicity. It decreased from 4.32b at x=0 to 3.95b at x=0.5 for the Fe system, 3.82b at x=1.0 for the Co system, 4.24b at x=0.1 for the Ni system, and 4.18b at x=0.1 for the Zn system, respectively. In addition, the structure distortion characteristic related to the change in the incommensurate modulation was examined with Raman scattering. The experimental data showed that the vibration properties of the oxygen atoms in both Bi-O and Sr-O bondings also changed with the decrease in the modulation periodicity. This behavior can be considered a consequence of structural relaxation caused by the enhancement of the degree of crystal misfit. \textcopyright{} 1996 The American Physical Society.

Determination of the Incommensurate Modulated Structure of Bi2Sr1.6La0.4CuO6+δ by Aberration-Corrected Transmission Electron Microscopy

A study of one‐dimensional incommensurate modulated structure determination in high‐resolution transmission electron microscopy

A Study of an Incommensurately Modulated Structure in Ca0.28Ba0.72Nb2O6by Electron Microscopy

Transmission Electron Microscopy Study of One-Dimensional Incommensurate Structural Modulation in Superconducting Oxides Bi2+xSr2−xCuO6+δ(0.10≤x≤0.40)

Compositional Evolution of the Anti-phase Stripe Superstructure in Bi2Sr2-xLaxCuO6 (0<x<=1.1) Revealed by Transmission Electron Microscopy

Modulation Structure Inbi2sr1.8

Transmission Electron Microscopy Study of La-Doped Bi-Sr-Cu-O Compound

Electron Crystallographic Study of Bi-4(Sr0.75la0.25)(8)Cu5oy Structure

Direct Visualization of Soliton Stripes in the CuO2 Plane and Oxygen Interstitials in Bi2(

Modulation Structure In Bi(2)Sr(1.8)La(0.2)Cu(1-X)M(X)O(Y) (M=Fe,Co,Ni, And Zn)

The Local Structure of Bismuth Strontium Copper Iron Oxide (Bi2.2sr1.8cu1-Xfexoy) Single Crystals Determined by Scanning Tunneling Microscopy

Spatially correlated incommensurate lattice modulations in an atomically thin high-temperature Bi_{2.1}Sr_{1.9}CaCu_{2.0}O_{8+δ} superconductors

Modulation structure in Bi2Sr1.8La0.2Cu1-xM xOy, (M=Fe, Co, Ni, and Zn)

Direct Visualization Of Soliton Stripes In The Cuo2 Plane And Oxygen Interstitials In Bi-2(Sr2-Xlax)Cuo6+Delta Superconductors

A new aspect of the structural modulation in crystal Bi2Sr2CaCu2Oy

Reconstruction of the Bi$_2$Sr$_2$CaCu$_2$O$_{8+δ}$ Fermi Surface

Characterization of Modulation Structure Inla2cuo4.12by Electron Diffraction

Observation Of The Modulated Structure In Bi2sr2cacu2oy Single-Crystals By Using An X-Ray Rotating-Anode Diffractometer

X-RAY DIFFRACTION STUDY OF THE MODULATED STRUCTURE IN Bi2Sr2CaCu2Oy SINGLE CRYSTALS

Direct Observation Of Incommensurate Modulation In Phase-Separated Cu-Rich La2cuo4.003

The Incommensurate Structure of High-Tcsuperconductors in the Bi-Sr-Ca-Cu-O System