In Situ Study of Formation Kinetics of Au Nanoclusters During HCl and Dodecanethiol Etching
Yang Lina,Huang Li,Song Xueyang,He Wenxue,Jiang Yong,Sun Zhihu,Wei Shiqiang
DOI: https://doi.org/10.3866/pku.whxb201801084
2018-01-01
Acta Physico-Chimica Sinica
Abstract:Gold nanoclusters are promising materials for a variety of applications because of their unique "superatom" structure, extraordinary stability, and discrete electronic energy levels. Controlled synthesis of well-defined Au nanoclusters strongly depends on rational design and implementation of their synthetic chemistry. Among the numerous approaches for the synthesis of monodisperse Au nanoclusters, etching of pre-formed polydisperse clusters has been widely employed as a top-down method. Understanding the formation mechanism of metal nanoclusters during the etching process is important. Herein, we synthesized monodisperse Au-13(L-3)(2)(SR)(4)Cl-4 nanoclusters via an etching reaction between polydisperse 1,3-bis(diphenylphosphino) propane (L-3)-protected polydisperse Au-n (15 <= n <= 60) clusters and a mixed solution of HCl/dodecanethiol (SR). The Au-13 product, with a mean size of (1.1 +/- 0.2) nm, shows pronounced step-like multiband absorption peaks centered at 327, 410, 433, and 700 nm. The synthetic protocol has a suitable reaction rate that allowss for real-time spectroscopic studies. We used a combination of in situ X-ray absorption fine structure (XAFS) spectroscopy, UV-Vis absorption spectroscopy, and matrix-assisted laser desorption ionization mass-spectrometry (MALDI-MS) to study the kinetic formation process of monodisperse Au-13 nanoclusters. Emphasis was given to the detection of reaction intermediates. The study revealed that the size-conversion of the Au-13 nanoclusters can be divided into three stages. In the first stage, the polydisperse Au-15-Au-60 clusters, covering a wide m/z range of 3000-13000, are prominently decomposed into smaller Au-8-Au-11 (within a m/z range of 3000-4000) species owing to the etching effect of HCl. They are immediately stabilized by the absorbed SR, L-3, and Cl- ligands to form metastable intermediates, as indicated by the high intensity of the Au-ligand coordination peak at 0.190 nm as well as the low intensity of the Au-Au peaks (0.236 and 0.288 nm) in the Fourier-transform (FT) EXAFS spectra. In the second stage, these Au-8-Au-11 intermediates are grown into Au13 cores. The experimental X-ray absorption near-edge spectra, totally different from that of Au(I)-SR polymer, could be well reproduced by the calculated spectrum of the Au13P8Cl4 cluster. The Au-ligand coordination number (1.0) obtained from the EXAFS fitting is much closer to the nominal values in Au-13(L-3)(2)(SR)(4)Cl-4 (0.92) than to that in Au(I)-SR polymers (2.0), suggesting that majority of the Au atoms are in the form of Au-13 clusters. The driving force for this growth process is primarily the geometric factor to form a complete icosahedral Au-13 skeleton through the incorporation of Au(I) ions or Au(I)-Cl oligomers pre-existing in the solution. In the third stage, the composition of the clusters is nearly unchanged as indicated by the MALDI-MS and the UV-vis spectra; however, their atomic structure undergoes rearrangement to the energetically stable structure of Au-13(L-3)(2)(SR)(4)Cl-4. During this structural rearrangement, the central-peripheral and peripheral-peripheral Au-Au bond lengths (RAu-Au(c-p) and RAu-Au(p-p)) decrease from 0.272 to 0.267 nm and 0.295 to 0. 289 nm, respectively, resulting in considerable structural distortion of the original icosahedral Au-13 skeleton. This distortion is also reflected by the slightly increased disorder degree of the Au-Au bonds from 0.00015 to 0.00017 nm(2). This work expands our understanding of the kinetic growth process of metal nanoclusters and promotes design and synthesis of metal nanomaterials in a controllable manner.