Abstract:Abstract Branches of ZnO nanostructure were hydrothermally grown on seed layer coated on sub-microrod template by ultrasonic-assisted immersion technique. Zinc acetate, monoethanolamine, and isopropanol were used as a precursor, stabilizer, and solvent for coating seed layer, respectively. The crystallization of seed layer, which was confirmed by x-ray diffractometer (XRD) and x-ray photoelectron spectrometer (XPS), was facilitated by ultrasonic irradiation. The sol concentration was adjusted to be 20 and 50 mM with the coating cycles of 8 and 16 for controlling the uniformity and surface energy of seed layer. The increase of sol concentration and coating cycles led to the increase of crystal orientation in (002) plane causing the improvement of seed layer’s surface energy which was estimated from water contact angle of the template. Atomic force microscope (AFM) was revealed that the seed layer did not cover the template only at the lowest condition of both sol concentration and coating cycles. However, the roughness and maximum peak-to-valley value tended to be increased for other conditions and dropped for the last condition which was suitable to vertically grow branches. After the growth of branches, the morphology of hierarchical ZnO nanostructure was investigated by field-emission scanning electron microscope (FESEM). It was found that the branches were vertically grown on the surface of rod template in every condition except the lowest sol concentration and coating cycles. Moreover, when the sol concentration and coating cycle of seed layer were increased, the branch density was also increased.

Growth Mechanism and Properties of Multibranched ZnO Nano/Microstructure

Preparation and Photoluminescence of ZnO with Nanostructure by Hollow-Cathode Discharge

Nanostructured ZnO: from Monodisperse Nanoparticles to Nanorods

Growth And Characterization Of Cu-Catalyzed Zno Nanowires

Synthesis of Branched Zno Nanorods on Various Substrates Via A Wet-Chemistry Route

In situ growth, structure characterization, and enhanced photocatalysis of high-quality, single-crystalline ZnTe/ZnO branched nanoheterostructures.

Branches of ZnO nanostructure grown on sub-microrod template with seed layer coated by ultrasonic-assisted immersion technique: effect of surface energy on the growth of branches

Growth Of Zno Crystals With Branched Spindles And Prismatic Whiskers From Zn-3(Oh)(2)V2o7 Center Dot H2o Nanosheets By A Hydrothermal Route

Formation Mechanism of Hollow Microspheres Consisting of ZnO Nanosheets

Growth and Properties of Nano ZnO

Controllable Synthesis and Characterization of Tube Brush-Like ZnO Nanowires Produced Via a Simple Chemical Vapor Deposition Method

Straight and Thin ZnO Nanorods: Hectogram-Scale Synthesis at Low Temperature and Cathodoluminescence.

Tempererature-Controlled Growth Of Zno Nanostructures: Branched Nanobelts And Wide Nanosheets

Hierarchical Construction of ZnO Architectures Promoted by Heterogeneous Nucleation

Growth and Formation Mechanism of C-Oriented ZnO Nanorod Arrays Deposited on Glass

Preparation and characterization of bat-like ZnO micro- and nanorods by adjusting oxygen flux

Growth mechanism and diameter control of well-aligned small-diameter ZnO nanowire arrays synthesized by a catalyst-free thermal evaporation method.

The Synthesis and Crystallography of Some Novel ZnO Nano- and Micro-Crystals and Structures

Hydrothermal Synthesis and Optical Properties of ZnO Nanostructured Films Directly Grown From/on Zinc Substrates

Brush-shaped ZnO heteronanorods synthesized using thermal-assisted pulsed laser deposition.

Nano/Micro-Structured ZnO Rods Synthesized by Thermal Chemical Vapor Deposition with Perpendicular Configuration