Abstract:In this paper, we report facile and efficient preparation of poly(propargyl quinolinium bromide) (PPQB) and poly(propargyl acridinium bromide) (PPAB). Both PPQB and PPAB are conjugated polymers with polyacetylene as backbones. Besides, they are polyelectrolytes since the side groups of PPQB and PPAB are quaternized quinolinium and acridinium, respectively. Therefore, PPQB and PPAB are conjugated polyelectrolytes, which are promising in many important applications. PPQB was prepared by reaction of the mixture of propargyl bromide (PB) and quinoline in DMF at 60 degrees C for 100 h. PPAB was synthesized under the same conditions via the same process except that acridine was used in the place of quinoline. The preparations are very simple and efficient, which need no any catalyst or initiator. The as-prepared PPQB and PPAB were characterized by elemental analysis and GPC-MALLS. Elemental analysis confirmed that PPQB and PPAB were the respective homopolymers of propargyl quinolinium bromide (PQB) and propargyl acridinium bromide (PAB). The molecular weights of the PPQB and PPAB were measured to be 1.8x10(5) and 8.1x10(4) g/mol, respectively, indicating efficient polymerizations of the respective monomers PQB and PAB. A tentative mechanism for the polymerizations was proposed as follows: firstly, the tertiary amine group of quinoline or acridine was quaternized by PB, leading to activation of the carbon-carbon triple bonds of the resultant quaternized salt; then, the nucleophilic attack on the triple bonds by pyridine resulted in carbon anions, which initiated the anionic polymerization of the quaternized salt. Furthermore, fluorescent and conductive properties of PPQB and PPAB were studied. Fluorescent measurements revealed that both PPQB and PPAB solutions had relatively strong fluorescent emissions, and the conductivity measurements demonstrated good conductivities of PPQB and PPAB films. Compared with poly(propargyl pyridinium bromide) that we reported previously, PPQB and PPAB are much less hygroscopic when exposed to air, so that PPQB and PPAB films are stable in the air. This broadens the applications of the two polymers.

Preparation and Characterization of PAQR Polymers by Different Methods

Synthesis of Polyacene Quinone Radical Polymers by Solvothermal Method

Synthesis Of Polyacene Quinone Radical Polymers With Controllable Conductivity And Their Electrorheological Behavior

Synthesis and Characterization of Amphiphilic Centipede-Like Copolymer PS-PS-PMAA

Synthesis of polyacene quinone radical polymers with controllable conductivity and their smart electrorheological behavior

Atom Transfer Radical Polymerization of Styrene with 2‐(1‐bromoethyl)‐anthraquinone As an Initiator

Structure/Conductivity Relationship of Polyacene Quinone Radical Polymers

Hollow PAQR Nanostructure and Its Smart Electrorheological Activity

Electrical-Properties of Polymer Composites - Conducting Polymer-Polyacene Quinone Radical Polymer

The Electrical and Electrorheological Properties of Grafted Polyacene Quinone Radical Polymers Dispersed in Silicone Oil

Preparation and Characterization of Single-Component Poly-α-olefin Oil Base Stocks

Structure and Properties of Poly-α-olefins Containing Quaternary Carbon Centers

Synthesis and characterization of poly(aryl ether ketone)s containing silican

Experimental and Computational Investigation of Oxidative Quenching Governed Aqueous Organocatalyzed Atom Transfer Radical Polymerization

Thermal Degradation Behaviors of Poly (arylene Ether Nitrile) Bearing Pendant Carboxyl Groups

Poly(aryl ether ketone)s with bromomethyl groups: Synthesis and quaternary amination

Synthesis of Polyelectrolytic Polyacetylene Derivatives by Quaternization of Poly(pyridylacetylene)

Facile and Efficient Catalyst-Free Preparation of Poly(propargyl Quinolinium Bromide) and Poly(propargyl Acridinium Bromide) and Characterizations of Their Structures and Properties

Synthesis and Characterization of Acetylene-Terminated Polybenzoxazines Based on Polyaralkyl-Phenolic Prepolymer

Synthesis, Characterization, and Thermal Pyrolysis Mechanism of High Temperature Resistant Phenolphthalein-Based Poly (arylene Ether Nitrile)

Rheokinetics and Rheological Properties of an Amphoteric Hydrophobic Quadripolymer Solutions