Novel yellowish‐green single‐phased spinel Mg1−xBaxAl2O4:Mn2+ phosphor(s) for color rendering white‐light‐emitting diodes
Qurat Ul Ain,Tanzeela Fazal,Shahid Iqbal,Sajid Mahmood,Bushra Ismail,Mazloom Shah,Asad Muhammad Khan,Ali Bahadur,Khalid M. Alotaibi,Matar Alshalwi
DOI: https://doi.org/10.1002/bio.4724
IF: 2.613
2024-03-26
Luminescence
Abstract:Current study is an effort to design a simple, single phase and cost‐effective material with the tunable emission of primary colors by series of MgAl2O4:Ba2+, Mn2+ nanopowders. Doped samples were found to have lower bandgaps compared with MgAl2O4. Due to Mn2+ and Ba2+'s larger ionic radius than Mg2+ and Al3+'s, shifting to higher 2θ from the reference peaks was seen. The synthesized derivatives of Mg1‐x‐0.3MnxBa0.3Al2O4 demonstrated that these yellowish‐green‐emitting phosphor. For white light‐rendering research activities, interpretation by using colored emitting materials is an alternative approach. But there are issues in designing the white color emitting materials. Particularly, differences in thermal and decay properties of discrete red, green, and blue emitting materials led to the quest for the search of a single‐phased material, able to emit primary colors for white light generation. The current study is an effort to design a simple, single‐phase, and cost‐effective material with the tunable emission of primary colors by a series of Mg1−xBaxAl2O4:Mn2+ nanopowders. Doping of manganese ion (Mn2+) in the presence of the larger barium cation (Ba2+) at tetrahedral‐sites of the spinel magnesium aluminate (MgAl2O4) structure led to the creation of antisite defects. Doped samples were found to have lower bandgaps compared with MgAl2O4, and hybridization of 3d‐orbitals of Mn2+ with O(2p), Mg(2s)/Al(2s3p) was found to be responsible for narrowing the bandgap. The distribution of cations at various sites at random results in a variety of electronic transitions between the valance band and oxygen vacancies as well as electron traps produced the antisite defects. The suggested compositions might be used in white light applications since they have three emission bands with centers at 516 nm (green), 464 nm (blue) and 622 nm (red) at an excitation wavelength of 380 nm. A detailed discussion to analyze the effects of the larger cationic radius of Ba2+ on the lattice strain, unit cell parameters, and cell volumes using X‐ray diffraction analysis is presented.
chemistry, analytical