Detailed investigation on microstructure and strengthening contribution of Al- x Cu-1.3Li-X alloy sheets
Guang-jun Zeng,Hao-ran Li,San-xi Deng,Peng-cheng Ma,Yong-lai Chen,Tian-le Liu,Jin-feng Li,Dan-yang Liu,Guo-fu Xu
DOI: https://doi.org/10.1016/j.matchar.2023.113278
IF: 4.537
2023-09-14
Materials Characterization
Abstract:The microstructure-mechanical properties connection and strengthening contribution of Al- x Cu-1.3Li-X ( x = 3.8, 4.2, 4.5 wt%) alloy sheets subjected to various heat treatments were systematically investigated. After solid-solution treatment, the decreased schmid factor value was the main factor for higher strength of Alloy-3 (4.5 wt% Cu). The number density and diameter of T 1 precipitates simultaneously increased with rising the Cu content during T8 aging, leading to the highest strength (655.4 MPa) of T8-aged Alloy-3. However, the high Cu content level resulted in the preferential precipitation of Guinier-Preston (G.P) zones during T6 aging at 165 °C. The θ' precipitates were therefore significantly increased and the nucleation of T 1 precipitates was suppressed in T6-aged Alloy-3, causing the reduced strength compared to that of T6-aged Alloy-2 (4.2 wt% Cu). Furthermore, the experimental yield strength was successfully predicted by invoking the modified precipitate strengthening model, in which the θ' precipitate-dislocation interaction was by-passing mechanism, whereas the shearable and by-passed T 1 precipitates coexisted for all alloys. The strengthening transition from by-passing to shearing occurred in T 1 precipitates with a thickness <1.9 nm or diameter <65 nm, and was particularly associated with the decrease in thickness of T 1 precipitates.
materials science, multidisciplinary,metallurgy & metallurgical engineering, characterization & testing