Leaching Reaction of Manganese Dioxide from Tantalum Capacitor Scrap - A Study on the Recycling of High Quality Rare Metal Secondary Resource.

Yuezhou WEI,Nobuaki SATO,Toshihide TAKENAKA,Michio NANJO

DOI: https://doi.org/10.2473/shigentosozai.105.181

1989-01-01

Shigen-to-Sozai

Abstract:A new process was proposed for the recycling of Ta capacitor scrap containing about 4-7% of MnO2as solid electrolyte. This paper describes the removal leaching of MnO2with various reductive agents, and moreover, disscuses the dissolution reactions of MnO2in FeSO4-H2SO4aqueous solution from both thermodynamic and kinetic aspects. The results are summarized as follows:1) In the leaching of block Ta anode scrap, H2O2and Na2SO3solution were the most effective leaching agents with more than 90% of Mn extraction at room temperature after 24 hours.2) When the sample was ground to-200 mesh, MnO2was almost completely removed in a short time by use of H2O2solution, cheap FeSO4solution also showed satisfactory result.3) In the dissolution reactions of MnO2with FeSO4-H2SO4solution, primary and secondary periods were observed. The reaction rate of primary was in proportion to [Fe2+] 0.65, and [H+] 0, while the reaction rate of secondary showed the dependency of [Fe2+] 0.45 and [H+] 0.25 The activation energies for primary and secondary were 4.6 kJ/mole and 5.1 kJ/mole respectively.4) The overall reaction of primary was seemed to be controlled by a mass transfer of Fe2+ions through the boundary layer between the solution and the surface of MnO2inside the capacitor, while dissolution of Fe (OH) 3 and other reaction products was the rate determining step in the secondary.5) Hermetic seal type Ta capacitor scraps were graded up by applying the Fe3+/Fe2+oxidative-reductive consistent leaching method.