Abstract:Nanosized transition metal oxides (TMOs) are one class of the most potential candidates for supercapacitors due to their short electron transport channels and reversible redox reactions. However, their easy-aggregation characteristics and volume shrinkage/expansion during the charge/discharge process seriously limit the practical application. To address this issue, in this work, a two-step thermal conversion different from traditional approaches is reported to synthesize tightly aligned Co3O4/carbon materials. The architecture of cross-linked nanosheets and uniformly distributed Co3O4 nanoparticles (NPs) is obtained by in-situ reduction of cobalt cations in flake-like zeolitic imidazolate frameworks (ZIFs) within inert gas at 500 degrees C and subsequent mild oxidation of metallic cobalt NPs to Co3O4 NPs (Co304@C-500). As a result, this strategy effectively prevents structural collapse and defect formation, which are usually caused by direct oxidation of ZIF-67 nanosheets. In supercapacitor tests, Co3O4@C-500 shows an appreciable specific capacitance (703.3 F g(-1) at 1 A g(-1)) and excellent cycling stability with the capacitance retention of 100% after 10,000 cycles at 10 A g(-1). Moreover, the Co3O4@C-500//reduced graphene oxide (RGO) asymmetric supercapacitor (ASC) exhibits an energy density of 43.99 Wh kg(-1) at a power density of 824.8 W kg(-1), and excellent cycling performance with a capacity retention of 88% after 10,000 cycles. Such excellent performance might benefit from the rational composition control and unique structure of Co3O4 NPs embedded in the carbon skeleton, which results in short electrolyte diffusion channels as well as electron transport distance and effectively reduce negative effect of volume change of electrode materials during the charge/discharge process.

Preparation of Nanocrystalline Co3O4 and Its Properties As Supercapacitors

Reviews and Prospectives of Co3O4-Based Nanomaterials for Supercapacitor Application

Electrochemical Capacitance Study on Co 3 O 4 Nanowires for Super Capacitors Application

Preparation of three-dimensional Co3O4@NiMoO4 nanorods as electrode materials for supercapacitors

Controllable synthesis of Co 3 O 4 from nanosize to microsize with large-scale exposure of active crystal planes and their excellent rate capability in supercapacitors based on the crystal plane effect

Preparation Of Mesoporous Nanocrystalline Co3o4 And Its Applicability Of Porosity To The Formation Of Electrochemical Capacitance

Cobalt Oxide Nanoparticles Embedded in N-Doped Porous Carbon as Efficient Electrode for Supercapacitor

Controllable Synthesis of Mesoporous Co3o4 Nanostructures with Tunable Morphology for Application in Supercapacitors

Sub-3 nm Co3O4 nanofilms with enhanced supercapacitor properties.

Synthesis of 3D-Nanonet Hollow Structured Co3O4 for High Capacity Supercapacitor

A Facile Low-Temperature Synthesis of Highly Distributed and Size-Tunable Cobalt Oxide Nanoparticles Anchored on Activated Carbon for Supercapacitors

Facile and green synthesis of mesoporous Co3O4 nanocubes and their applications for supercapacitors.

Facile fabrication of porous Co3O4 nanowires for high performance supercapacitors

Engineering of Co3O4 electrode via Ni and Cu-doping for supercapacitor application

Facile synthesis of 3D gem shape Co3O4 with mesoporous structure as electrode for high-performance supercapacitors

Three-Dimensional Nanoscale Co3o4 Electrode On Ordered Ni/Si Microchannel Plates For Electrochemical Supercapacitors

Enhanced Electrochemical Performance of Ball Milled Coo for Supercapacitor Applications

Nanostructured (co, Mn)3O4 for High Capacitive Supercapacitor Applications

Ethanol-assisted Solvothermal Synthesis of Porous Nanostructured Cobalt Oxides (coo/co3o4) for High-Performance Supercapacitors

Highly stable Co<sub>3</sub>O<sub>4</sub> nanoparticles/carbon nanosheets array derived from flake-like ZIF-67 as an advanced electrode for supercapacacitor

Preparation and performance of Co3O4–NiO composite electrode material for supercapacitors