Abstract:The aim of this study is to prepare highly ordered porous anodic alumina (PAA) with large pore sizes (u003e 200 nm) by an improved two-step anodization approach which combines the first hard anodization in oxalic acid-water-ethanol system and second mild anodization in phosphoric acid-water-ethanol system. The surface morphology and elemental composition of PAA are characterized by field emission scanning electron microscopy (FESEM) and energy-dispersive X-ray spectrometer (EDS). The effects of matching of two-step anodizing voltages on the regularity of pore arrangement is evaluated and discussed. Moreover, the pore formation mechanism is also discussed. The results show that the nanopore arrays on all the PAA samples are in a highly regular arrangement and the pore size is adjustable in the range of 200-300 nm. EDS analysis suggests that the main elements of the as-prepared PAA are oxygen, aluminum and a small amount of phosphorus. Furthermore, the voltage in the first anodization must match well with that in the second anodization, which has significant influence on the PAA regularity. The addition of ethanol to the electrolytes effectively accelerates the diffusion of the heat that evolves from the sample, and decreases the steady current to keep the steady growth of PAA film. The improved two-step anodization approach in this study breaks through the restriction of small pore size in oxalic acid and overcomes the drawbacks of irregular pore morphology in phosphoric acid, and is an efficient way to fabricate large diameter ordered PAA.

Fabrication of Ordered Porous Anodic Alumina with Ultra-Large Interpore Distances Using Ultrahigh Voltages

Highly Ordered Porous Anodic Alumina with Large Diameter Pores Fabricated by an Improved Two-Step Anodization Approach

Fabrication of Crystallized Porous Anodic Aluminum Oxide under Ultra-High Anodization Voltage

Self-Ordered Porous Anodic Alumina with Large Pore Intervals: Review on Experimental and Theoretical Research

Fabrication of highly ordered porous anodic alumina membrane with ultra-large pore intervals in ethylene glycol-modified citric acid solution

Fabrication of highly ordered nanoporous alumina films by stable high-field anodization

Fabrication of porous anodic alumina membranes with ultrathick barrier layer

Investigation on Highly Ordered Porous Anodic Alumina Membranes Formed by High Electric Field Anodization

High-Speed Growth and Photoluminescence of Porous Anodic Alumina Films with Controllable Interpore Distances over A Large Range

Fabrication of Porous Anodic Alumina Films by Using Two-Step Anodization Process

Fabrication of Porous Alumina Templates with a Large-Scale Tunable Interpore Distance in a H 2 C 2 O 4 -C 2 H 5 OH-H 2 O Solution

A new self-ordering regime for fast production of long-range ordered porous anodic aluminum oxide films

Evolution Process of Orderly Nanoporous Alumina by Constant High Field Anodization in Oxalic Acid Electrolyte

Fast Fabrication of Highly Ordered Porous Anodic Alumina Membranes by Hard-mild Anodization

A Highly Controllable Electrochemical Anodization Process to Fabricate Porous Anodic Aluminum Oxide Membranes

Fabrication of porous anodic alumina (PAA) templates with straight pores and with hierarchical structures through exponential voltage decrease technique

A New Method for Highly Efficient Fabrication of Through-Hole Porous Anodic Alumina Membranes

Facile Fabrication of Ordered Anodized Aluminum Oxide Membranes with Controlled Pore Size by Improved Hard Anodization

Fabrication and Application of Alumina Nanoscale Ordered Array Template

A Controllable and Widely Applicable Electrochemical Anodization Process to Fabricate Porous Anodic Aluminum Oxide Membrane

Electrochemical Fabrication Of Novel Nanostructures Based On Anodic Alumina