Abstract:In this study, Nickel nanoparticles/reduced graphene oxide was successfully prepared through an in-situ hydrothermal process by applying graphene oxide as a precursor that was applied as a catalyst for converting CO2 into CH4. NiNPs/rGO were characterized using UV-Vis spectrophotometer, Fourier Transform Infrared (FTIR), X-Ray Diffraction (XRD), Scanning Electron Microscope (SEM), and Energy-Dispersive X-Ray Spectroscopy (EDS). The characterization of the UV-Vis spectrophotometer shows NiNPs/rGO gave absorption at 260 nm which indicates red shifting from GO absorption peak (230 nm). FTIR spectra of NiNPs/rGO shows a decreasing in absorbance from the peaks of the oxygen-containing group (i.e. carboxylic and hydroxyl group) previously contained in the GO, moreover disappearance of the absorption peak at 1736 cm−1 (C=O) in NiNPs/rGO also indicates that reduction process from GO into rGO has been successfully carried out. The construction of Nickel nanoparticles on the surface of the rGO was proven from the results of EDX (% mass) shows the presence of C (21.84 %), O (5.58 %), and Ni (72.58 %) on the surface of NiNPs (30 %)/rGO. In its application as catalysts, the NiNPs (30 %)/rGO catalysts have shown a good activity in the process of CO2 methanation (i.e. CO2 conversion into CH4). Initial catalytic test had been done to evaluate the effect of reaction temperature on CO2 methanation using NiNPs (30 %)/rGO as catalyst. The catalytic test result shows that catalys could produce methane as the main product with highest value of 17.63 % at 673 K.

Preparation of two-dimensional NiO/graphene composite and superior catalytic activity in benzene hydrogenation

Preparation of Sno2/Graphene Nanocomposite and Its Application to the Catalytic Epoxidation of Alkenes with H2o2

One‐Pot Synthesis of a Highly Active 3‐dimensional Fe−Nx−CNTs/rGO Composite Catalyst for Oxygen Reduction

Preparation of graphene supported nickel nanoparticles and their application to methanol electrooxidation in alkaline medium

One-step Chemical Vapor Synthesis of Ni/graphene Nanocomposites with Excellent Electromagnetic and Electrocatalytic Properties

Enhanced catalytic hydrogenation activity of Ni/reduced graphene oxide nanocomposite prepared by a solid-state method

Graphene Supported Nano Particles of Pt–Ni for CO Oxidation

Synthesis of Fe2O3/rGO/N-rGO Catalyst and Its Application in Selective Hydrogenation of Nitrobenzene

N-Doped Graphene-Supported Diatomic Ni–Fe Catalyst for Synergistic Oxidation of CO

Ni-promoted synthesis of graphitic carbon nanotubes from in situ produced graphitic carbon for dehydrogenation of ethylbenzene

Atomically Dispersed Cu Anchored on Nitrogen and Boron Codoped Carbon Nanosheets for Enhancing Catalytic Performance

Synthesis of Ni/GO-TiO2 composites for the photocatalytic hydrogen production and CO2 reduction to methanol

Synthesis of Pt-Ni/graphene Via in Situ Reduction and Its Enhanced Catalyst Activity for Methanol Oxidation.

Preparation of Ni/CNTs Catalyst with High Reducibility and Their Superior Catalytic Performance in Benzene Hydrogenation

Fixation of Nitrogen to Ammonia with Photocatalytic on Petroleum Pitch-Based Graphene Oxide Supported Nickel/Nickel Oxide Composite Catalyst

In situ conversion of Co–CoN nanowires into ultrathin 2D nanosheets for highly effective catalytic hydrogenation

Ni nanoparticles supported on graphene layers: An excellent 3D electrode for hydrogen evolution reaction in alkaline solution

Interfacial interaction of amorphous NiFe hydroxide/graphene composites elevating the oxygen evolution catalytic performance

Noble-Metal-Free Ni(Oh)(2)-Modified Cds/Reduced Graphene Oxide Nanocomposite with Enhanced Photocatalytic Activity for Hydrogen Production under Visible Light Irradiation

2D/2D-Ni–Co–B/rGO Nanolayers Prepared by Galvanic Replacement for Hydrogen Generation through NaBH 4 Hydrolysis

In-situ hydrothermal synthesis of nickel nanoparticle/reduced graphene oxides as catalyst on CO2 methanation